LiFePO4/C composite cathode materials were synthesized by a novel carbothermal reduction(CTR) method using glucose as carbon resource. The precursors and the products were characterized by TG-DTA, XRD, TEM, and the reaction mechanism was investigated. The electrochemical performance of the samples was measured. The results show that the new method can reduce synthesis temperature, and the sample prepared at 600℃ for 24h can deliver a discharge capacity of 156mAh·g-1 at 0.05C. The first discharge capacities of LiFePO4 at 0.1C, 0.2C, 1C are 146mAh·g-1, 135mAh·g-1, 130mAh·g-1, 121mAh·g-1, respectively. It retains discharge capacity of 119mAh·g-1 at 1C after 30 cycles, with only 1.56% capacity decrease.
LIU Su-Qin
,
GONG Ben-Li
,
ZHANG Ge
,
LI Shi-Cai
. Synthesis of LiFePO4/C Composite Cathode Materials by a Novel Carbothermal Reduction Method and Its Performance[J]. Journal of Inorganic Materials, 2007
, 22(2)
: 283
-286
.
DOI: 10.3724/SP.J.1077.2007.00283
[1] Padhi A K, Nanjundaswamy K S, Goodenough J B. J. Electrochem. Soc.,1997,144 (4):1188--1194.
[2] Andersson A S, Kalska B, Haggstrom, et al. Solid State Ionics,2000,130 (1-2):41.
[3] Yamada A, Chung S C, Hinokuma K. J. Electrochem. Soc.,2001,148 (3):A224--229.
[4] Huang H, Yin S C, Nazar L F. Electrochem. Solid-State Lett.,2001,4 (10):A170--172.
[5] Franger S, LeCras F, Bourbon C, et al. J. Power Sources,2003,119-121:252--257.
[6] 卢俊彪, 唐子龙, 张中太(LU Jun-Biao, et al). 无机材料学报(Journal of Inorganic Materials), 2005,20 (3):666--670.
[7] Yang S F, Zavalij P Y, Whittingham M S. Electrochemistry Communicatuions,2001,3:505--508.
[8] Tajimi S, Ikeda Y, Uematsu K, et al. Solid State Ionics,2004,175:287--290.
[9] 张静, 刘素琴, 黄可龙, 等. 无机化学学报, 2005,21 (5):433--436.
[10] Jingsi Yang, Xu J. J. Electrochemical and Solid-State Letters,2004,7 (12):A515--518.
[11] Piana M, Cushing B L, Goodenough J B, et al. Solid State Ionics, Diffusion & Reactions,2004,175 (1-4):30.
[12] Miran G, Robert D, Marjan B, et al. Solid State Ionics,2005,176 (19-22):1801--1805.
[13] Park K S, Son J T, Chung H T, et al. Electrochemistry Communications,2003,5:839--842.
[14] Park K S, Kang K T, Lee S B, et al. Materials Research Bulletin,2004,39:1803--1810.
[15] Arnold G, Garche J, Hemmer R, et al. J. Power Sources,2003,119-121:247--251.
[16] Cho T H, Chung H T. J. Power Sources,2004,113:272--276.
[17] Myung S T, Komaba S, Hirosaki N, et al. Electrochimica Acta,2004,49:4213--4222.
[18] Higuchi M, Katayama K, Azuma Y, et al. J. Power Sources,2003,119-121:258--261.
[19] Baker J, Saidi M Y, Swoyer J L. Electrochem. Solid-State Lett,2003,6 (3):A53--A55.
[20] 徐峙晖, 赖琼玉, 吉晓洋. 四川大学学报(工程科学版), 2005,37 (4):77--80.