Mechanical-activation-assisted combustion synthesis of SiC was conducted with PVC and/or NH4Cl as promoters. The mechanical activation of the Si-C reactants through high-energy attrition milling results in substantial decrease of the ignition temperature and the incubation time for the Si-C combustion reaction. Ultra-fine β-SiC powders with equiaxed grains can be synthesized at the preheating temperature as low as 1050C. The specific surface area (SSA) of the combustion synthesized SiC powders is 4.36m2/g, and the average particle size is less than 5μm.
YANG Kun
,
YANG Yun
,
LIN Zhi-Ming
,
LI Jiang-Tao
. Mechanical-Activation-Assisted Combustion Synthesis of SiC[J]. Journal of Inorganic Materials, 2007
, 22(2)
: 263
-267
.
DOI: 10.3724/SP.J.1077.2007.00263
[1]Hu J Q, Lu Q Y, Tang K B, et al. Chem. Mater., 1999, 11 (9): 2369--2371.
[2]陈立富(CHEN Li-Fu). 无机材料学报(Journal of Inorganic Materials), 1994, 9 (4): 465--470.
[3]乔冠军, 金志浩. 硅酸盐通报, 1993, 3: 34--39.
[4]μnir Z A, Anselmi-Tamburini U. Mater. Sci. Rep., 1989, 3 (7): 277--365.
[5]Pamesh P D, Vaidhyanathan B, Ganguli M, et al. J. Mater. Res., 1994, 9 (12): 3025--3027.
[6]Pampuch R, Stobierski L, Lis J, et al. Mat. Res. Bull., 1987, 22 (9): 1225--1231.
[7]王铁军,王声宏(WANG Tie-Jun, et al).硅酸盐学报(Journal of the Chinese Ceramic Society), 1998, 26 (2): 237--242.
[8]Yamada O, Hirao K, Koizumi M. J. Am. Ceram. Soc., 1991, 72 (9): 1735--1738.
[9]Yamamoto T A, Ishii T, Kodera Y, et al. J. Ceram. Soc. Jpn., 2004, 112 (5): s940--s945.
[10]Kharatyan S L, Nerisisyan H H. Key Eng. Mater., 2002, 217: 83--92.
[11]蔡海荣, 陈大英, 李江涛(CAI Hai-Rong, et al). 硅酸盐学报(Journal of the Chinese Ceramic Society), 2002, 30 (3): 393--397.
[12]Mossino P. Ceram. Int., 2004, 30: 311--332.
[13]Takacs L. Progr. Mater. Sci., 2002, 47: 355--414.
[14]Jin H B, Yang Y, Chen Y X, et al. J. Am. Ceram. Soc., 2006, 89 (3): 1099--1102.
[15]Lee W C, Chung S L. J. Mater. Res., 1997, 12 (3): 805--811.
[16]Nersisyan G A, Nikogosov V N, Kharatyan S L. Combust. Expl., Shock Waves., 1992, 28 (3): 251--254.
[17]Hermann H, Schubert T, Gruner W, et al. Nanostruct. Mater., 1997, 8 (2): 215--229.