Potassium titanate nanofibers ( K1.34H0.66Ti2O4(OH)2) were prepared by using ion-exchange reaction between KOH solution and titanic acid nanotube (H2Ti2O4(OH)2). TEM and XRD results show that the nanotubes change into nanofibers and the crystalline structure alters. K/Ti atomic ratio, chemical state of K and Ti elements for the product were determined by means of atomic absorption spectrophotometry, colorimetric method, and X-ray photoelectron spectroscopy. The results indicate that the empirical formula of the product is K1.34H0.66Ti2O4(OH)2. Compared with H2Ti2O4(OH)2 nanotubes, the thermal-stability of potassium titanate nanofibers is higher. At T>700℃, the crystalline structure of this material changes into monoclinic phase K2Ti4O9. High temperature treatment results in nanofibers’ sizes increasing, but the aspect ratio is still high. The BET surface area of the material is 104m 2·g-1.
WANG Xiao-Dong
,
JIN Zhen-Sheng
,
ZHANG Jing-Wei
,
YANG Jian-Jun
,
ZHANG Zhi-Jun
. Preparation and Characterization of Potassium Titanate Nanofiber[J]. Journal of Inorganic Materials, 2007
, 22(2)
: 237
-242
.
DOI: 10.3724/SP.J.1077.2007.00237
[1] Halberstadt M L, Rhee S K, Mansfield J A. Wear, 1978, 46 (1): 109--126.
[2] Kim S J, Cho M H, Lim D S, et al. Wear, 2001, 251 (1-12): 1484--1491.
[3] Tjong S C, Meng Y Z. Polymer, 1998, 39 (22): 5461--5466.
[4] Yu D M, Wu J S, Zhou L M, et al. Composites Science and Technology, 2000, 60 (4): 499--508.
[5] Kasuga T, Hiramatsu M, Hoson A, et al. Langmuir, 1998, 14 (12): 3160--3163.
[6] 张顺利, 周静芳, 张治军, 等. 科学通报, 2000, 45 (10): 1533--1536.
[7] YANG J J, JIN Z S, WANG X D, et al. Dalton Trans. 2003, (20): 3898--3901.
[8] SUN X M, Li Y D. Chem. Eur. J., 2003, 9 (10): 2229--2238.
[9] Ma R, Bando Y, Sasaki T. Chemical Physics Letters, 2003, 380 (5-6): 577--582.
[10] ZHU H Y, GAO X P, LAN Y, et al. J. Am. Chem. Soc., 2004, 126 (27): 8380--8381.
[11] MENG X D, WANG D Z, LIU J H, et al. Materials Research Bulletin, 2004, 39 (14-15): 2163--2170.
[12] YUAN Z Y, SU B L. Colloids and Surfaces A: Physicochem. Eng. Aspects, 2004, 241 (1-3): 173--183.
[13] 付敏, 江志东, 马紫峰, 等(FU Min, et al). 无机材料学报(Journal of Inorganic Materials), 2005, 20 (4): 808--814.
[14] ZHU H Y, LAN Y, GAO X P, et al. J. Am. Chem. Soc., 2005, 127 (18): 6730--6736.
[15] Hodos M, Horv\acute ath E, Haspel H, et al. Chemical Physics Letters, 2004, 399 (4-6): 512--515.
[16] WANG B L, CHEN Q, HU J, et al. Chemical Physics Letters, 2005, 406 (1-3): 95--100.
[17] WANG B L, CHEN Q, WANG R H, et al. Chemical Physics Letters, 2003, 376 (5-6): 726--731.
[18] YUAN Z Y, ZHANG X B, SU B L. Appl. Phys. A, 2004, 78 (7): 1063--1066.
[19] SUN X M, CHEN X, LI Y D. Inorg. Chem., 2002, 41 (20): 4996--4998.
[20] 王晓冬, 李伟, 杨建军, 等. 化学研究, 2003, 14 (2): 5--8.
[21] Wagner C D, Riggs W M, Davis L E, et al. Handbook of X-Ray Photoelectron Spectroscopy, Perkin-Elmer Corporation,
Eden Prairie, Minnesota, 1979.
[22] ZHANG M, JIN Z S, ZHANG J W, et al. Journal of Molecular Catalysis A : Chemical, 2004, 217 (1-2): 203--210.
[23] Joint Committee on Powder Diffraction Standard, 32--0861.