New organic-inorganic nanocomposite materials of collagen and modified TiO2 were prepared. The change of content of collagen in the nanocomposites along with the alteration of temperature and pH value was studied, and the influence of such factors as types of TiO2 crystals, Al2O3 films of modification on TiO2 and cross-link with glutaraldehyde on the infrared emissivity of the composites was investigated. The results indicate that the optimal temperature and pH value for the reaction between collagen and modified nanosized TiO2are 50℃ and 8.0 respectively, under which the content of collagen increases up to 9.45wt%. The nanocomposites are endowed with much lower infrared emissivity and the thermal stability of the nanocomposite materials is enhanced greatly due to the strong interactions between collagen and modified nanosized TiO2. After being cross-linked by glutaraldehyde, disorderly distributional nanocomposites are turned to regular and ordered laminar netty ones, which improves the tensility and stability of the materials and lowers the infrared emissivity further to 0.502.
SUN Yan-Qing
,
ZHOU Yu-Ming
. Preparation and Characterization of Collagen/TiO2 Nanocomposite with Low Infrared Emissivity[J]. Journal of Inorganic Materials, 2007
, 22(2)
: 227
-231
.
DOI: 10.3724/SP.J.1077.2007.00227
[1] 宋兴华, 於定华, 马新胜, 等. 红外技术, 2003, 25 (6): 49--53.
[2] 李浩宏, 陈之荣, 李俊篯, 等. 化学学报, 2005, 63 (8): 697--703.
[3] 周钰明, 单云, 曹勇, 等. 高等学校化学学报, 2004, 25 (5): 966--970.
[4] Lebeau Benedicate, Sanchez Clement. Current Opinion in Solid State & Materials Science, 1999, 4 (1): 11--23.
[5] 吴腊英, 李长江. 无机化学学报, 2002, 18 (4): 400--401.
[6] 谢刚, 朱华山, 张皓东, 等. 昆明理工大学学报, 2004, 29 (4): 39--42.
[7] 于志强, 武高辉, 孙东立, 等(YU Zhi-Qiang, et al). 无机材料学报(Journal of Inorganic Materials), 2003, 18 (6): 1250--1254.
[8] 姚超, 高国生, 林西平, 等(YAO Chao, et al). 无机材料学报(Journal of Inorganic Materials), 2006, 21 (2): 315--321.
[9] 戴光平. 四川兵工学报, 1996, 17 (4): 2--3.
[10] 潘逴, 赵振声, 何华辉. 华中科技大学学报(自然科学版), 2003, 31 (7): 28--30.