Study on the Synthesis and Properties of Superparamagnetic Monodisperse Fe3O4 Nanoparticles
Received date: 2008-11-20
Revised date: 2008-12-27
Online published: 2009-07-20
There are extensive applications for superparamagnetic Fe3O4 nanoparticles in the field of biomaterials. Superparamagnetic magnetite nanoparticles coated with oleic acid were prepared in the refluxing mixed system of water, ethanol alcohol and toluene at 74℃. The effect of the OH- concentration on the surface properties, size, dispersion and magnetic properties of magnetite nanoparticles was studied systematically. The properties of magnetite nanoparticles were tested by X-ray diffraction (XRD), fourier transform infrared (FTIR), dynamic light scattering (DLS), transmission electron microscopy (TEM) and vibrating sample magnetometer (VSM). The results show that when the molar ratio of NaOH to Fe(Ⅱ) is less than 8, magnetite nanoparticles coated with oleic acid can be dispersed easily in nonpolar solvents. The addition of NaOH has no obvious influence on the size and the saturation magnetization of magnetite nanoparticles. While the molar ratio of NaOH to Fe(Ⅱ) is more than 8, magnetite nanoparticles can only be dispersed in polar solvents, such as water. Although the saturation magnetization increases to 40A·m2/kg, magnetite nanoparticles are polydisperse and easy to agglomerate in water.
Key words： magnetite nanoparticles; superparamagnetic; monodisperse
JIANG Wen , WEN Xian-Tao , WANG Wei , WU Yao , GU Zhong-Wei . Study on the Synthesis and Properties of Superparamagnetic Monodisperse Fe3O4 Nanoparticles[J]. Journal of Inorganic Materials, 2009 , 24(4) : 727 -731 . DOI: 10.3724/SP.J.1077.2009.00727
［1］Laurent Sophie, Forge Delphine, Port Marc, et al. Chem. Rev., 2008, 108(6):2064-2110.
［2］Bao Jie, Chen Wei, Liu Taotao, et al. ACS Nano.,2007,1(4):293-298.
［3］Liong Monty, Lu Jie, Kovochich Michael, et al. ACS Nano., 2008,2(5):889-896.
［4］Sahoo Sanjeeb K, Labhasetwar Vinod. Drug Discovery Today,2003,8(24):1112-1120.
［5］Jordan Andreas, Scholz Regina, Wust Peter, et al. Journal of Magnetism and Magnetic Materials, 1999,201(1/2/3): 413-419.
［6］Kim D K, Zhang Y, Voit W, et al. Journal of Magnetism and Magnetic Materials, 2001,225(1/2): 30-36.
［7］Sun Shouheng, Zeng Hao, Robinson David B, et al. J. Am. Chem. Soc., 2004, 126(1): 273-279.
［8］Vidal-Vidala J, Rivas b J, L′opez-Quintela M A. Colloids and Surfaces A: Physicochem. Eng. Aspects, 2006, 288(1/2/3): 44-51.
［9］Massart R. IEEE Trans. Magn., 1981,MAG-17(2): 1247-1248.
［10］Shen L, Laibinis P E, Hatton T A. Langmuir, 1999,15(2): 447-453.
［11］Hyeon Taeghwan, Lee Su Seong, Park Jongnam. J. Am. Chem. Soc., 2001, 123(51): 12798-12801.
［12］Rockenberger Jorg, Scher Erik C, Alivisatos A Paul. J. Am. Chem. Soc., 1999, 121(49): 11595-11596.
［13］Wen Xiantao, Yang Junxiao, He Bin, et al. Current Applied Physics, 2008, 8(5): 535-541.
［14］Hong R Y, Zhang S Z, Han Y P. Powder Technology, 2006, 170(1): 1-11.
［15］López-Quintela M Arturo, Rivas José. Journal of Colloid and Interface Science, 1993, 158(2): 446-451.
［16］刘 冰, 王德平, 黄文旵, (LIU Bing, et al)等. 无机材料学报(Journals of Inorganic Materials), 2008, 23(1): 33-38.
［17］Liu Xianqiao, Kaminski Michael D, Guanc Yueping. Journal of Magnetism and Magnetic Materials, 2006, 306(2): 248-253.
［18］倪星元, 沈 军, 张志华. 纳米材料的理化特性与应用. 北京：化学工业出版社, 2006: 53-55.
［19］Tao Ke, Dou Hongjing, Sun Kang. Colloids and Surfaces A: Physicochem. Eng. Aspects, 2006, 290(1/2/3): 70-76.
［20］Jun Young-Wook, Seo Jung-Wook, Cheon Jinwoo. Accounts of Chemical Research, 2008, 41(2): 179-189.
［21］Zhang Ling, He Rong, Gu Hong-Chen. Applied Surface Science, 2006,253(5): 2611-2617.
/
| 〈 |
|
〉 |