Sol-Gel Preparation of Titania/Organic Silicone Hybrid Thin Films

  • WANG Fang ,
  • LUO Zhong-Kuan ,
  • QING Shuang-Gui ,
  • QIU Qi ,
  • SHI Yong
Expand
  • (College of Chemistry and Chemical Engineering, Shenzhen University, Shenzhen 518060, China)

Received date: 2009-04-16

  Revised date: 2009-07-14

  Online published: 2010-01-24

Abstract

Incorporation of metal alkoxides into polymers through Sol-Gel process is of significant interest for tuning the refractive index of optical materials. The organic-inorganic hybrid material with tunable refractive index (RI) and high transparency was studied. Tetrabutoxytitanate (TBOT) and alkoxysilanes including diphenyldimethoxysilane (DPS) and γ-Glycidoxypropy1 trimethoxysilane (GPTS) were employed as sources of the titania sol and the silica sol respectively. Subsequently, crack-free films were fabricated by spin coating. The hybrid films with different Ti contents were characterized by various techniques including IR, UV-Vis, TG/DSC, TEM and auto-laser ellipsometer. The results indicated that the hybrid films displayed homogeneous morphology and titania was crosslinked with alkoxysilanes. The RI of films increased from 1.54 to 1.64 at 633nm with Ti molar fraction varing from 10% to 70%. And the transmittances of the hybrid films in the visible range were higher than 90%.

Key words: Sol-Gel; titania; hybrid films

Cite this article

WANG Fang , LUO Zhong-Kuan , QING Shuang-Gui , QIU Qi , SHI Yong . Sol-Gel Preparation of Titania/Organic Silicone Hybrid Thin Films[J]. Journal of Inorganic Materials, 2010 , 25(1) : 37 -40 . DOI: 10.3724/SP.J.1077.2010.00037

References

[1]Blanc D, Last A, Franc J, et al. Thin Solid Films, 2006, 515(3): 942-946.
[2]O’Brien S, Copurog^lu M, Crean G M. Thin Solid Films, 2007, 515(13): 5439-5443.
[3]Copurog^lu M, O’Brien S, Crean G M. Polymer Degradation and Stability, 2006, 91(12): 3185-3190.
[4]O’Brien S, Copurog^lu M, Crean G M. Appl. Surf. Sci., 2007, 253(19): 7969-7972.
[5]Copurog^lu M, O’Brien S, Crean G M. J. SolGel Sci. Techn., 2006, 40(1): 75-82.
[6]Uricanu V, Donescu D, Banu A G, et al. Mater. Chem. Phys., 2004, 85(1): 120-130.
[7]熊明娜, 周树学, 陈 辉, 等. 高分子学报, 2005(3): 417-422.
[8]Chen W C, Liu W C, Wu P T, et al. Mater. Chem. Phys., 2004, 83(1): 71-77.
[9]Sarwar M I, Zulfiqar S, Ahmad Z. J. SolGel Sci. Technol., 2007, 44(1): 41-46.
[10]Chang C M, Chang C L, Chang C C. Macromol. Mater. Eng., 2006, 291(12): 1521-1528.
[11]Tsai M, Liu S, Chiang P. Thin Solid Films, 2006, 515(3): 1126-1131.
[12]Xiong M, Zhou S, You B, et al. J. Polym. Sci. : Part B: Polym. Phys., 2005, 43(6): 637-649.
[13]Wang Y, Zhang D, Shi L, et al. Mater. Chem. Phys., 2008, 110(2/3): 463-470.
[14]Guan C, Lü C L, Liu Y F, et al. J. Appl. Polym. Sci., 2006, 102(2): 1631-1636.
[15]Que W X, Zhou Y, Lam Y L, et al. Thin Solid Films, 2000, 358(1/2): 16-21.
[16]Que W X, Zhou Y, Lam Y L, et al. Thin Solid Films, 2000, 359(2): 177-183.
[17]Que W X, Hu X. Thin Solid Films, 2003, 436(2): 196-202.
[18]江 梅, 刘毅飞, 吕长利, 等. 高分子学报, 2008(6): 594-599.
[19]罗仲宽, 刘剑洪, 田德余(LUO Zhong-Kuan, et al). 无机材料学报(Journal of Inorganic Materials), 2004, 19(2): 367-372.
[20]黄世强, 孙争光, 李盛彪, 等. 新型有机硅高分子材料. 北京: 化学工业出版社, 2004: 141-156.
[21]Wang S, Xia G, He H, et al. J. Alloy. Compd., 2007, 431(1/2): 287-291.
Outlines

/