Journal of Inorganic Materials

Journal of Inorganic Materials >

2009 , Vol. 24 >Issue 3: 457 - 462

DOI: https://doi.org/10.3724/SP.J.1077.2009.00457

Research Paper

Preparation of Ti-Zr-V-O Catalytic Composite Material and its Selective Catalytic Reduction of NO

  • SHEN Yue-Song ,
  • ZHU She-Min ,
  • QIU Tai ,
  • SHEN Shu-Bao
Expand
  • 1. College of Material Science and Engineering, Nanjing University of Technology, Nanjing 210009, China; 2. College of Life Science and Pharmaccutical Engineering, Nanjing University of Technology, Nanjing 210009, China

Received date: 2008-09-01

  Revised date: 2008-10-14

  Online published: 2009-05-20

Fold

Abstract

A series of Ti-Zr-V-O catalytic composite materials were prepared by sol-gel method. Effect of doping zirconium on catalytic NOx activities of Ti-V-O composite catalysts was investigated, and effects of doping zirconium on crystal form, crystalline morphology, chemical composition, functional group structure and specific surface area of titanium-vanadium composite oxides were characterized by X-ray diffraction (XRD), Scanning electron microscope (SEM), Energy spectrum analysis (EDS), Fourier infrared spectrum (FT-IR) and N2 physical adsorption (BET method) respectively. The experimental results show that doping zirconium can inhibit anatase crystalline transformation, refine grain size, change the crystalline morphology and enhance the solid acidity of Ti-V-O composite catalysts. Consequently, the catalytic properties of Ti-Zr-V-O composite catalysts are improved. In the process of selective catalytic reduction of NO over Ti-Zr-V-O/ATS ceramics monolithic catalysts, using NH3 as reducing agent, doping zirconium widens the catalytic active zone to high temperature area about 100℃, and the highest NO conversion at 300℃ is increased by 17.3%.

Key words： Ti-Zr-V-O catalytic composite materials; sol-gel; doping zirconium; deNOx

Cite this article

SHEN Yue-Song , ZHU She-Min , QIU Tai , SHEN Shu-Bao . Preparation of Ti-Zr-V-O Catalytic Composite Material and its Selective Catalytic Reduction of NO[J]. Journal of Inorganic Materials, 2009 , 24(3) : 457 -462 . DOI: 10.3724/SP.J.1077.2009.00457

References

［1］鞠振树. 科技情报开发与经济, 2006, 20(16): 135-136.
［2］李振中. 中国科技产业, 2006, (2): 48-52.
［3］童志权. 工业废气净化与利用. 北京: 化学工业出版社, 2001: 287-289.
［4］钟 秦. 燃煤烟气脱硫脱硝技术及工程实例. 北京: 化学工业出版社, 2002: 284-284.
［5］Pio Forzatti. Appl. Catal. A:General, 2001, 222(1-2): 221-236.
［6］Zhu S M, Shen Y S, Wang J L, et al. J. Rare Earth, 2007, 25(4):457-461.
［7］韩承辉，刘炳华，张惠良，等. 物理化学学报, 2006, 22(8): 993-998.
［8］Yang J, Ferreira J M F. Materials Research Bulletin, 1998, 33(3): 389-394.
［9］曲虹霞，钟 秦. 环境科学与技术, 2004, 27(6): 23-24.
［10］陆佩文. 无机材料科学基础. 武汉: 武汉理工大学出版社, 2001:67-67.
［11］杨南如，岳文海. 无机非金属材料图谱手册. 武汉: 武汉工业大学出版社, 2000: 281-316.
［12］孙克勤. 选择性催化还原脱硝的理论及实验研究. 南京理工大学博士论文, 2007.
［13］毛东森，卢冠忠，陈庆龄. 催化学报, 2004, 25(6): 501-510.
［14］喻 瑶，林 涛，张丽娟，等(Yu Yao, et al). 无机材料学报(Journal of Inorganic Materials), 2008, 23(1): 71-76.
［15］Prvulescu V I, Boghosian S, Parvulescu V, et al. J. Catal., 2003, 217(1): 172-185.
［16］Lahousse C, Aboulayt A, Maugé F, et al. J. Mol. Catal., 1993, 84(3): 283-297.
［17］Kitiyanan Athapol, Yoshikawa Susumu. Mater. Lett., 2005, 59(29-30): 4038-4040.
Options
Outlines

/

〈 〉