The defect chemistry of BaPbO3 was studied by the measurement of the equilibrium electrical conductivity as a function of oxygen pressure (10-12-105 Pa). The major defects and their charge-compensating defects in undoped and acceptor-doped BaPbO3 were present. The influence of impurities concentrations on equilibrium electrical conductivity and both inflexions of the change of major defects in high and low oxygen-activity regions were discussed. At highly oxygen activity the major defects are lead vacancies and their compensating holes. With the decreasing in oxygen activity, the major defects will change from intrinsic disorder into
extrinsic disorder and the acceptor impurities become the major source of defects. At lower oxygen activity the oxygen vacancies become compensating defects instead of the holes, and the reducing reaction becomes the major source of compensating defects. Both inflexions in high and low oxygen-activity regions move to higher oxygen activity with the increasing of acceptor concentrations.
LU Yu-Dong
,
WANG Xin
,
ZHUANG Zhi-Qiang
,
LIU Bao-Ling
,
LIU Yong
. Nonstoichiometry in Acceptor-doped BaPbO3 [J]. Journal of Inorganic Materials, 2007
, 22(5)
: 811
-815
.
DOI: 10.3724/SP.J.1077.2007.00811
[1] Chang M C, Wu J M, Cheng S Y, et al. Materials Chemistry and Physics, 2000, 65: 57--62.
[2] 陆裕东, 王歆, 庄志强(LU Yu-Dong, et al). 无机材料学报(Journal of Inorganic Materials), 2007, 22 (1): 138--142.
[3] Luo Yih-Rong, Wu Jenn-Ming. Applied Physics Letters, 2001, 79 (22): 3669--3671.
[4] Wang X, LU Y D, Zhuang Z Q. Journal of the Chinese Ceramics Society, 2006, 34 (9): 1140--1142.
[5] Luo Yih-Rong, Wu Jenn-Ming. Jpn. J. Appl. Phys., 2003, 42: 242--246.
[6] 陆裕东, 王歆, 庄志强. 功能材料与器件学报, 2007, 13 (1): 13--16.
[7] Yasukawa M, Kadota A, Maruta M, et al. Solid state Communications, 2002, 124: 49--52.
[8] 陆裕东, 王歆, 庄志强(LU Yu-Dong, et al). 硅酸盐学报(Journal of the Chinese Ceramics Society), 2007, 35 (3): 308--311.
[9] 王歆, 陆裕东, 庄志强(WANG Xin, et al). 硅酸盐学报(Journal of the Chinese Ceramics Society), 2007, 35 (6): 696--700.
[10] Smyth D M. J. Electroceram., 2002, 9: 179--186.
[11] Chan N H, Sharma R K, Smyth D M. J. Electrochem. Soc., 1981, 128 (8): 1762--1769.
[12] Chan H N, Sharma R K, Smyth D M. J. Am. Ceram. Soc., 1982, 65 (3): 167--170.
[13] Smyth D M. Solid State Ionics, 2000, 129: 5--12.