Joining Strength and Microstructure of Sintered SiC/SiC Joints Prepared by Active Brazing Process

  • LIU Yan ,
  • HUANG Zheng-Ren ,
  • LIU Xue-Jian ,
  • CHEN Jian
Expand
  • 1.Shanghai Institute of Ceramics, Chinese Academy of Sciences, Shanghai 200050, China; 2.Graduate University of the Chinese Academy of Sciences, Beijing 100049, China

Received date: 2008-06-19

  Revised date: 2008-09-03

  Online published: 2009-03-20

Fold

Abstract

Sintered SiC ceramics were brazed with itself by ternary Ag-Cu-Ti filler metal foil. Effects of brazing parameters such as temperature, holding time on joining strength, together with interface microstructure and reaction products were investigated. Experimental results indicate that joining strength has peak value with the increasing of brazing temperature and holding time, and the max fourpoint bending strength of SiC/SiC joints reaches 342MPa. The joining strength increases first with the increasing of brazing temperature and holding time due to thickening of the reaction layer, then decreases due to evaporation of the filler metal. A uniform compact reaction layer of about 1μm thickness is found at the interface between SiC and filler metal, which is formed by the reaction of active element Ti of filler metal and SiC substrate. TiC and Ti5Si3 are confirmed as the reactive products by XRD and EDX.

Key words： Ag-Cu-Ti filler metal; SiC; joining strength; microstructure

Cite this article

LIU Yan , HUANG Zheng-Ren , LIU Xue-Jian , CHEN Jian . Joining Strength and Microstructure of Sintered SiC/SiC Joints Prepared by Active Brazing Process[J]. Journal of Inorganic Materials, 2009 , 24(2) : 297 -300 . DOI: 10.3724/SP.J.1077.2009.00297

References

［1］Li J Q, Zhu G M, Xiao P. J. Mater. Sci. Lett., 2003, 22(10): 759-761.
［2］Prakash P, Mohandas T, Raju P D. Scripta Mater.,2005, 52(11): 1169-1173.
［3］Lee H L, Nam S W, Hahn B S, et al. J. Mater. Sci., 1998, 33(20): 5007-5014.
［4］Singh M. J. Mater. Sci. Lett., 1998, 17(6): 459-461.
［5］Zhang J, Zhou Y, Naka M. Trans. Nonferrous Met. China, 2005, 15(4): 261-265.
［6］GB/T6569-2006, 精细陶瓷弯曲强度实验方法.
［7］Boadi J K, Yano T, Iseki T. J. Mater. Sci., 1987, 22(7): 2431-2434.
［8］程兰征，章燕豪.物理化学. 上海：上海科学技术出版社，1987：251-252.
［9］Naka M, Feng J C,Schuster J C. Metall. Mater. Trans.A, 1997, 28A: 1385-1390.
Options
Outlines

/

〈 〉