The effect of surface residual stress and crack on bending strength of reaction bonded silicon carbide (RBSiC) after grinding was investigated. The residual stress of the ground surfaces were determined using X-ray diffraction.The sizes of strength controlling cracks were assessed using fracture mechanics approach. The investigations show that mechanical load, which has relation with grinding direction, phays a dominateve role in the grinding processes. and the measured residual stresses have a direction dependency. With increase of down feed from 0.9μm/s to 1.35μm/s, the bending strength is reasonably correlated with the surface residual stress and crack size.
YAO Wang
,
ZHANG Yu-Min
,
HAN Jie-Cai
,
ZHA Yan-Feng,ZHOU Yu-Feng
,
HAN Yuan-Yuan
,
QU Wei
. Effect of Grinding Induced Damage on Bending Strength of RBSiC[J]. Journal of Inorganic Materials, 2009
, 24(2)
: 301
-304
.
DOI: 10.3724/SP.J.1077.2009.00301
[1]黄清伟, 高积强, 金志浩. 西安交通大学学报, 2000, 34(2): 89-90.
[2]Robichaud J, Guregian J, Schwalm M. SiC optics for Earth observing applications. Earth Observing Systems VIII. Proc. SPIE 5151, 2003: 53-62.
[3]Tobin E, Magida M, Kishner S. Design, fabrication, and test of a meterclass reactionbonded SiC mirror blank. Silicon carbide materials for optics and precision structures. Proc. SPIE 2543, 1995: 12-21.
[4]Gopal A V, Rao P V. International Journal of Machine Tools and Manufacture, 2003, 43(13): 1327-1336.
[5]Zhang Y M, Zhang J H, Han J C, et al. Materials Letters, 2004, 58(7): 1204-1208.
[6]Bandyopadhyay B P, Ohmori H. International Journal of Machine Tools & Manufacture, 1999, 39(5): 839-853.
[7]朱洪涛, 林 滨, 吴 辉, 等. 精密制造与自动化,2004,2: 15-18.
[8]王西彬, 李相真.金刚石与磨料磨具工程, 1997, 6(102): 18-23.
[9]Eigenmann B, Macherauch E. Nuclear Instruments and Methods in Physics Research B, 1995, 97(1): 92-97.
[10]Immelmann S, Welle E, Reimers W. Material Science and Engineering A, 1997, 238(2):287-292.
[11]Genzel C, Klaus M, Denks I. Material Science and Engineering A, 2005, 390(1): 376-384.
[12]Yang H T, Gao L, Yuan R Z, et al. Materials Chemistry and Physics, 2003, 80(1): 305-308.
[13]李伯民,赵 波. 实用磨削技术. 北京: 机械工业出版社, 1996: 42-49.
[14]Tomba A G, Cavalieri A L. Materials Research Bulletin, 2000, 35(7): 1077-1085.
[15]Roberts S G, Lawrence C W, Bisrat Y. J. Am. Ceram. Soc., 1999, 82(7):1809-1816.
[16]Li K, Liao T W. Journal of Materials Processing Technology, 1996, 57(3): 207-220.