Journal of Inorganic Materials

Journal of Inorganic Materials >

2009 , Vol. 24 >Issue 2: 353 - 356

DOI: https://doi.org/10.3724/SP.J.1077.2009.00353

Research Paper

Coprecipitation Synthesis and Oxide Ionic Conductivities of Ce0.8Sm0.2O1.9-based Nanocomposite Materials

  • ZHANG Hong ,
  • ZHANG Zhe ,
  • MA Guo-Qiang ,
  • ZHANG Yu-Xing ,
  • LI Zhi-Cheng
Expand
  • School of Materials Science and Engineering, Central South University, Changsha 410083, China

Received date: 2008-07-04

  Revised date: 2008-09-07

  Online published: 2009-03-20

Fold

Abstract

Ce0.8Sm0.2O1.9-La9.33Si6O26 nanocomposite materials were prepared by a two-step coprecipitation synthesis process. Phases and microstructure were investigated by X-ray diffraction and transmission electron microscope. Conductivities were measured by an A.C. impedance measurement system. The results show that the calcined nanocomposites have average grain size of 20nm and the sintered bulks have average grain size of 44nm. The oxideion conductivity of the nanocomposite material is 0.25Ω/cm at 700℃.The conductivities of the nanocomposites are 3 orders higher than that of pure La9.33Si6O26 ceramics, which are also higher than that of Ce0.8Sm0.2O1.9 conductor in the test temperatures range. The conducting mechanisms for the nanocomposite ionic conductors are discussed.

Key words： nanocomposite material; coprecipitation synthesis; oxide-ion conductivity

Cite this article

ZHANG Hong , ZHANG Zhe , MA Guo-Qiang , ZHANG Yu-Xing , LI Zhi-Cheng . Coprecipitation Synthesis and Oxide Ionic Conductivities of Ce0.8Sm0.2O1.9-based Nanocomposite Materials[J]. Journal of Inorganic Materials, 2009 , 24(2) : 353 -356 . DOI: 10.3724/SP.J.1077.2009.00353

References

［1］Hibino T, Inoue T, Tokuno J, et al. Science, 2000, 288: 2031-2033.
［2］Inaba H, Tagawa H. Solid State Ionics, 1996, 83(1-2): 1-16.
［3］Sansom J E H, Richings D, Slater P R. Solid State Ionics, 2001, 139(3-4): 205-210.
［4］Tolchard J R, Islam M S, Slater P R. J. Mater. Chem., 2003, 13(8): 1956-1961.
［5］Okudera H, Masubuchi Y, Kikkawa S, et al. Solid State Ionics, 2005, 176(15-16): 1473-1478.
［6］Li Z C, Zhang H, Bergman B. Ceram. Int., 2008, 34(8):1949-1953.
［7］Li G S, Li L P, Feng S H, et al. Advanced Mater., 1999, 11(2): 146-149.
［8］Maier J. Solid State Ionics, 2004, 175(1-4): 7-12.
［9］Tsoga A, Naoumidis A, Stover D. Solid State Ionics, 2000, 135(1-4): 403-409.
［10］Kosacki I, Rouleau C M, Becher P F, et al. Solid State Ionics, 2005, 176(13-14): 1319-1326.
［11］Jiang S S, Wanger J B. J. Phys. Chem. Solids, 1995, 56(8): 1101-1111.
［12］Liang C C. J. Electrochem. Soc., 1973, 120(10): 1289-1303.
Options
Outlines

/

〈 〉