Research Paper

Preparation and Characterization of α-Ni(OH)2/SiO2 Submicrosphere
and α-Ni(OH)2 Hollow Submicrosphere

  • LOU Zai-Liang ,
  • LI Qun-Yan ,
  • WANG Zhi-Hong ,
  • WEI Qi ,
  • NIE Zuo-Ren
Expand
  • College of Materials Science and Engineering, Beijing University of Technology, Beijing 100022, China

Received date: 2008-06-10

  Revised date: 2008-08-28

  Online published: 2009-03-20

Abstract

The nearly monodisperse SiO2 submicrospheres with uniform size (270nm) were prepared by the hydrolysis of TEOS. Then the SiO2 submicrospheres were coated with α-Ni(OH)2 nanoflakes by a new solution growth method. The Ni(OH)2 nanoflakes were synthesized by a solution process using hydrofluoric acid solution as nickel ion ligand to form nickel-fluoro complex, NH3 aqueous solution as OH- supplier and also supplemental nickel ion ligand. The coating thickness is increased with coating times. It is only 35nm for coating once. After coating three times, the coating thickness is increased to about 100nm. The α-Ni(OH)2 hollow submicrospheres are obtained after subsequent removal of the core particles by NaOH solution(20wt%) at 40℃ for 24h. BET calculation shows that the surface area of the Ni(OH)2 hollow spheres is 141.06m2/g.

Cite this article

LOU Zai-Liang , LI Qun-Yan , WANG Zhi-Hong , WEI Qi , NIE Zuo-Ren . Preparation and Characterization of α-Ni(OH)2/SiO2 Submicrosphere
and α-Ni(OH)2 Hollow Submicrosphere[J]. Journal of Inorganic Materials, 2009
, 24(2) : 345 -348 . DOI: 10.3724/SP.J.1077.2009.00345

References

[1]Fleming S, Mandal T K, Walt D R. Chem. Mater., 2001,13(6): 2210-2216.
[2]李志会, 杨修春, 杜天伦. 材料导报, 2007, 21(s1): 189-192.
[3]Dong A G, Wang Y J, Wang D G, et al. Microp. Mater., 2003, 64(1-3): 69-81.
[4]French H M, Henerson M J, Hillman A R, et al. Electroanal. Chem., 2001, 500(1-2): 192-207.
[5]刘元刚, 唐致远, 徐 强, 等. 化学进展, 2006, 18(7-8): 883-888.
[6]Liu X H, Yu L. J. Power Sources, 2004, 128(2): 326-330.
[7]Han X J, Xie X M, Xu C Q, et al. Opt. Mater., 2003, 23(1-2): 465-470.
[8]Jeevanandam P, Koltypin Y, Gedanken A. Nano Lett., 2001, 1(5): 263-266.
[9]Liang J H, Li Y D. Chem. Lett., 2003, 32(12): 1126-1130.
[10]Liang Z H, Zhu Y J, Hu X L. J. Phys. Chem. B, 2004, 108(11): 3488-3491.
[11]Yang D N, Wang R M, Zhang J, et al. J. Phys.Chem. B, 2004, 108(23): 7531-7533.
[12]Duan G T, Cai W P, Luo Y Y, et al. Adv. Funct. Mater., 2007, 17(6): 644-650.
[13]Liu J, Du S F, Wei L Q, et al. Materials Letters, 2006, 60(29-30): 3601-3604.
[14]Wang D B, Song C X, Hu Z S, et al. J. Phys. Chem. B, 2005, 109(3): 1125-1129.
[15]王汝娜,李群艳,王志宏, 等. 高等学校化学学报; 2008, 29(1): 18-22.
[16]Li Q Y, Wang R N, Nie Z R, et al. J. Colloid Interface Sci., 2008, 320: 254258.
[17]王汝娜,李群艳,王志宏, 等(WANG Ru-Na, et al). 无机材料学报(Journal of Inorganic Materials), 2007, 22(5): 889-893.
Outlines

/