In order to improve the polarization property of LSCN as an anode material of direct-hydrocarbon SOFC, the LSCN powder was mixed with nanometer SDC in weight ratio of 1:1. The conductivity and polarization properties of LSCN-SDC anode in H2 and CH4 atmospheres were examined and discussed, relating to the SEM morphologies. The interface structure between the anode and the YSZ electrolyte is obviously modified when nanometer SDC is added. The AC
impedance of the anode with SDC is only tenth of that without SDC, and the polarization property is greatly improved. After polarization test, no carbon species was observed from the microstructure morphology of the LSCN-SDC anode.
LI Song-Li
,
WANG Shao-Rong
,
NIE Huai-Wen
,
WANG Yuan-Song
,
WEN Ting-Lian
. La0.85Sr0.15Cr0.9Ni0.1O3-δCe0.8Sm0.2O1.9as an Anode Material of SOFC[J]. Journal of Inorganic Materials, 2006
, 21(5)
: 1121
-1126
.
DOI: 10.3724/SP.J.1077.2006.01121
[1] Finnerty C M, Coe N J, Cunningham R H, et al. Catal. Today, 1998, 46: 137--145.
[2] Yashiro K, Takeda K, Taura T, et al. In situ observation of deposited carbon on anode for solid oxide fuel cells. Eds. S.C. Singhal, M. Dokiya. in: Proceedings of the Eighth International Symposium on Solid Oxide Fuel Cells (SOFCVIII), Paris: The Electrochemical Society, 2003. 714--719.
[3] Abudula A, Ihara M, Komiyama H, et al. Solid State Ionics, 1996, 86--88: 1203--1209.
[4] Sauvet A L, Irvine J T S. Solid State Ionics, 2004, 167: 1--8.
[5] Sfeir J, Buffat P A, Mockli P, et al. J. Catal., 2001, 202: 229--244.
[6] Sfeir J, van herle J. McEvoy A J. J. Eur. Ceram. Soc., 1999, 19: 897--902.
[7] Eguchi K, Setoguchi T, Inoue T, et al. Solid State Ionics, 1992, 52: 165--172.
[8] Uchida H, Suzuki H, Watanabe M. J. Electrochem. Soc., 1998, 145: 615--620.
[9] Marina O A, Bagger C, Primdahl S, et al. Solid State Ionics, 1999, 123: 199--208.
[10] Gorte R J, Kim H, Vohs J M. J. Power Sources, 2002, 106: 10--15.
[11] Steele B C H, Middleton P H, Rudkin R A. Solid State Ionics, 1990, 40: 388--393.
[12] Minh N Q, Takahashi T. Science and Technology of Ceramic Fuel Cells Netherlands: Elsevier, Amsterdam 1995. 119.
[13] 查全性. 电极过程动力学理论, 第三版. 北京: 科学出版社, 2002. 272.
[14] Mori M, Hiei Y, Sammes N M. Solid State Ionics, 2000, 135: 743--748.
[15] Mori M, Yamamoto T, Ichikawa T. Solid State Ionics, 2002, 148: 93--101.
[16] Sfeir J, Van herle J, McEvoy A. J. Lanthanum chromite based anodes for methane oxidation. Eds. P. Stevens. In: Proceedings of the Third European Solid Oxide Fuel Cell Forum, Nantes-France, 1998. 267--276.
[17] Yoon S P, Han J, Nam S W, et al. J. Power Sources, 2002, 106: 160--166.
[18] Takeguchi T, Kani Y, Yano T, et al. Journal of Power Sources, 2002, 112: 588--595.