Based on PAAO's unique cellular hexagon morphology and composition, various alumina fibers (nano-belts, nano-rods, and nano-tubes) were fabricated by simply employing a dilute acid etching method. Scanning electron microscope (SEM) incorporated with energy dispersive X-ray spectroscope (EDS) and transmission electron microscope (TEM) were applied to characterize these nano-fibers. It is proved that alumina nano-fibers are formed from the porous layer, while totally different behaviors of the barrier layer and the porous layer are showed during the etching process. The orientated etching, resulted from PAAO's particular morphology and composition, is believed to be the main reason that explains the formation of different alumina nano-fibers.
PAN Jin-Zhi
,
ZHAO Hong
,
CHEN Chun-Huan
,
LI Guo-Jun
,
REN Rui-Ming
. Fabrication of Alumina Nano-fibers from PAAO[J]. Journal of Inorganic Materials, 2006
, 21(4)
: 828
-832
.
DOI: 10.3724/SP.J.1077.2006.00828
1 陈立富, 严勇军, 高桂英(Chen Li-Fu, et al). 硅酸盐学报(Journal of the Chinese Ceramic Society), 1997, 25(3): 339-343.
2 Venkatesh R, Royramanan S. Journal of the European Ceramic Society, 2000, 20: 2543-2549.
3 Harold G, Sowman L. Ceramic Bull., 1988, 67(12): 1911-1916.
4 Sumio Sakka. Am. Ceramic Soc. Bull., 1985, 64(11): 1463-1466.
5 Kostikov V I, Makhova M F, Sergeev V P. Ceramic Eng. Sci. Pro., 1994, 14: 557-566.
6 Bunsell A R, Berger M H. Key Eng. Mater., 1997, 15: 127-131.
7 Satishkumar B C, Govindaraj A, Vogl E M, et al. J. Mater. Res., 1997, 12: 604-610.
8 Tang C C, Fan C C, Li P, et al. J. Cryst. Growth, 2001, 224: 117-121.
9 Zou Jianping, Pu Lin, Bao Xiaomao, et al. App. Phy. Lett., 2002, 80(6): 1079-1081.
10 Xiao Z L, Han C Y , Welp U, et al. Nano Lett., 2002, 11(2): 1293-1297.
11 Liu S M, Zhang W D, liu Z L, et al. Applied Catalysis A: General, 2005, 287: 108-115.
12 Yuan Z H, Huang H, Fan S. Adv. Mater., 2002, 14: 303-306.
13 Tian Y T, Meng G W, Gao T, et al. Nanotechnology, 2004, 15: 189-191.
14 Thompson G E, Furneaux R C, ARichardson J. Nature, 1978, 272: 433-435.
15 Thompson G E, Wood G C. Nature, 1981, 290: 230-232.
16 Keller F, Hunter M S, Robinson D L. J. Electrochem. Soc., 1953, 100: 411-419.
17 Diggle J W, Downie T C, Groulding C W. Chem. Rev., 1969, 69: 365-405.
18 Pu Lin, Chen Zhiqiang, Tan Chao, et al. Chin. Phys. Lett., 2002, 19(3): 391-394.