Barium ferrite encapsulated porous glass particles(BEPG)were prepared with a citrate sol-gel method. The precursors were obtained from barium nitrate,citric acid and porous glass particles and then calcined at 850℃ for 2h with 60℃/h heating rate. The microstructure, complex dielectric constant, complex permeability and microwave absorption of the production were tested by X-ray diffraction, scan election microscope (SEM) and network analyzer. It was found that the BaFe12O19 crystal coated the porous glass particles surfaces well, which in turn exhibited the microwave absorption property. Microwave absorber coating of BEPG with 1.8mm thick was made with latex matrix and the reflection loss was more than -8dB at the range of 5～18GHz. The peak of reflection losses was -15dB at 6 GHz.
ZHANG Yan-Qing
,
ZHANG Xiong
. Preparation and Microwave Absorption Property of BaFe12O19 Encapsulated
Porous Glass Particles[J]. Journal of Inorganic Materials, 2006
, 21(4)
: 861
-866
.
DOI: 10.3724/SP.J.1077.2006.00861
1 宛德福, 马兴隆. 磁性物理学, 北京: 电子工业出版社, 1999. 301-418.
2 Choi S H, Oh J H, Ko T. Journal of Magnetism and Magnetic Materials, 2004, 272(3): 2233-2235.
3 阎鑫, 胡小玲, 岳红, 等．材料导报, 2001, 15(1): 62-64.
4 毛倩瑾, 于彩霞, 王群, 等．北京工业大学学报, 2003, 29(1): 108-111.
5 曾爱香, 熊惟浩, 王采芳．材料保护, 2004, 37(9): 19-20.
6 Giannakopoulou T, Kompotiatis L, Kontogeorgakos A, et al. Journal of Magnetism and Magnetic Materials, 2002, 246(3): 360-365.
7 张晏清. 同济大学学报, 2004, 32(2): 208-212.
8 张清敏, 徐濮编译. 扫描电子显微镜和X射线微区分析. 天津: 南开大学出版社, 1988. 198-212.