Low-cost C/SiC composites were prepared by “CVI+PIP”combined process. A silicone impregnant with fillers was used in the PIP process. The pyrolysis mechanism of the impregnant and the properties of the composites were investigated. The results show that silicone impregnant with fillers has high pyrolysis yield and its pyrolysis product is dense, pressure can enhance the PIP efficiency of the fillered impregnant. “CVI+ P-PIP” hybrid process makes use of the densification advantages of CVI process and PIP process, which can shorten the process cycle. C/SiC/C multilayered coating can decrease the bonding strength of the fiber/matrix interface, and it reduces the diffusing velocity of oxygen to the surface of carbon fibers. Hence the mechanical properties and anti-oxidation properties are improved. The flexural strength and fracture toughness (K IC) of the C/SiC composites are 455MPa and 15.7MPa·m-1/2 respectively. The weight loss of the C/SiC composites is merely 8.5% after heated at 1300℃ in air 3h.
YAN Lian-Sheng
,
LI He-Jun
,
CUI Hong
,
WANG Tao
. Low-cost C/SiC Composites Prepared by CVI+Pressure-PIP Hybrid Process[J]. Journal of Inorganic Materials, 2006
, 21(3)
: 664
-670
.
DOI: 10.3724/SP.J.1077.2006.00664
1 闫联生, 王涛, 邹武, 等. 宇航材崐料工艺, 1999, 29 (3): 38-41.
2 Yoshida K, Imai M, Yano T. Journal of the Ceramic Society of Japan, 2000, 108 (12): 224-229.
3 Ortona A. Donato A, Filacchioni G, et al. J. Fusion Engineering and Design, 2000, 51-52: 159-163.
4 Nannetti C A, Riccardi B, Ortona A. Journal of Nuclear Materials, 2002, 307-311 (2): 1196-1199.
5 马青松, 陈朝辉, 郑文伟, 等. 复合材料学报, 2003, 20 (2): 53--57.
6 Renlund G M, Prochazka S, Doremus R H. J M ater Res, 1991, 6 (12): 2723-2734.
7 Rangarajan S, Belardinelli R, A swath P B. J M ater Sci, 1999, 34 (3): 515-533.
8 简科, 胡海峰, 马青松, 等. 科学与工程学报, 2003, 21 (1): 13-16.
9 马青松, 陈朝辉, 郑文伟, 等. 中国有色金属学报, 2004, 14 (7): 1133-1138.
10 Takuya A, Hiroshi H, Taku H. Carbon, 2001, 39: 1477-1483.