SiC coated CNTs nano-composites were prepared by the conversion of the precursor polycarbosilane (PCS) and their microstructures were observed and analyzed by SEM, TEM and HRTEM. The electromagnetic parameters of the nano-composites were measured under the frequency from 2 to 18GHZ. Results
showed that uniform and compact SiC coatings on the surfaces of CNTs could be synthesized in the initial PCS/xylene concentration section of 10%～15%. The measurement of the electromagnetic parameters of SiC coated CNTs one-dimensional nano-composites indicated that the main electromagnetic loss mechanism was dielectric loss. When the initial PCS concentration was 15%, the SiC coated CNTs nano-composites had the highest dielectric coefficient and loss angle and the best electromagnetic wave absorption properties as well as the composite effects.
LIANG Tong-Xiang
,
ZHAO Hong-Sheng
,
ZHANG Yue
. Electromagnetic Wave Absorption Properties of SiC Coated CNTs Nano-composites[J]. Journal of Inorganic Materials, 2006
, 21(3)
: 659
-663
.
DOI: 10.3724/SP.J.1077.2006.00659
1 刘亚宁. 电磁生物效应. 北京 北京邮电大学出版社, 2002. 35-38.
2 Che Renchao, Li Yongqing. Journal of Materials Science, 1999, 18: 1963-1964.
3 Casady J B, Johnson R W, et al. Solid State Electronics, 1996, 39: 1409-1414.
4 葛凯勇, 王群, 张晓宁, 等. 功能材料与器件学报, 2002, 8: 263-266.
5 孙晶晶, 李建保, 张波, 等. 材料工程, 2003, 3: 43-47.
6 李黎明, 徐政. 江苏陶瓷, 2004, 37: 6-10.
7 高文, 冯志海, 黎义. 宇航材料工艺, 2000, 5: 1-5.
8 焦桓, 罗发, 周万城. 西北工业大学学报, 2002, 20: 172-175.