This paper described the tribological properties under different braking speeds of carbon/cabon composites whose microstructures are rough lamina, smooth lamina, mixture of rough lamina and smooth lamina respectively. Optical microscope and scanning electron microscope techniques were used to characterize the microstructures and the worn surfaces. The friction and wear properties of the composites were tested by using a laboratory dynamometer. Results indicate that the friction coefficients of the material a increase to the peak at 15m·s-1, while the friction coefficients of sample b and c increase to the peak at 20m·s-1. However, the same temperature of about 250℃ is showed under the worn surface 1mm when the friction coefficient increases to the peak. The weight loss increases with the increase of the braking speeds from 5m·s-1 to 30m·s-1, but the weight loss of 28m·s-1 is lower than that of 30m·s-1.
YU Shu
,
HUANG Bai-Yun
,
XIONG Xiang
,
ZHANG Chuan-Fu
. Tribological Properties under Different Braking Speeds of Carbon/Carbon Composites[J]. Journal of Inorganic Materials, 2006
, 21(3)
: 651
-658
.
DOI: 10.3724/SP.J.1077.2006.00651
1 Skopp A, Woydt M. Tribology Transactions, 1995, 38: 2-10.
2 Czichos H, Klaffke D, Santner E. Wear, 1995, 190: 155-161.
3 薛永春. 粉末冶金技术, 1991, 6(6): 5-7.
4 贺福, 王茂章, 碳纤维及其复合材料. 北京: 科学出版社, 1997. 257-258.
5 Erich Fitzer. Carbon, 1987, 25(2): 163-190
6 张福勤, 黄启忠, 邹林华(Zhang Fu-qin, et al). 无机材料学报(Journal of Inorganic
Materials), 2004, 19(5): 1118-1122.
7 廖寄乔, 黄伯云, 黄志锋等, 理化检验-物理分册, 2002, 38(11): 501-506.
8 Blanco C, Bermejo J, Marsh H. Wear, 1997, 213(1): 1-12.
9 Yen B K, Tadashi Ishihara. Carbon, 1996, 34(3): 489-498.
10 于澍, 刘根山, 李溪滨, 稀有金属材料与过程, 2003, 32(3): 213-215.
11 李江鸿. 硕士学位论文, 长沙: 中南大学. 2002.
12 徐惠娟, 熊翔, 黄伯云, 摩擦学学报, 2003, 23(4): 344-349.
13 Li C C. Int. Conf., ASME, NY, 1981. 525-533.