Effects of TeO2Additions on the Properties of Fluoroaluminate Glasses

  • FAN You-Yu ,
  • YUAN Xin-Qiang ,
  • FENG Ji-Tian ,
  • HU He-Fang
Expand
  • Shanghai Institute of Optics & Fine Mechanics, Chinese Academy of Sciences, Shanghai 201800, China

Received date: 2005-03-07

  Revised date: 2005-04-04

  Online published: 2006-03-20

Fold

Abstract

In order to improve the ability of fluoroaluminate glass against devitrification, TeO2 was introduced into fluoroaluminate glass with the molar composition of 10MgF2-20CaF2-10SrF2-10BaF215YF335AlF3. The influence of TeO2 content on the glass formability of fluoroaluminate was studied by differential thermal
analysis technique. And the glass structure analysis was performed by infrared
absorption spectra and Raman scattering spectra. The results indicate that
TeO2 can increase the crystallization onset temperature T xof glasses, decrease melting temperature T mof glasses and improve the ability against devitrification. The structure analysis indicates that,
with the increase of TeO2 content, the YF8polyhedral units decrease,
and more [FnAl--O--AlFn], [TeO3], [TeO2F] and [TeOF2] units exist in the glass network with the introduction of TeO2 which are bridged by the F-and O2-. With good glass forming ability, the
TeO2 modified fluoroaluminate glass also shows high transmittance in the
region of 0.4~5μm; therefore it is a new prospective infrared optical material.

Key words： telluride-fluoroaluminate glass; thermal stability,infrared transmittance,glass structure

Cite this article

FAN You-Yu , YUAN Xin-Qiang , FENG Ji-Tian , HU He-Fang . Effects of TeO2Additions on the Properties of Fluoroaluminate Glasses[J]. Journal of Inorganic Materials, 2006 , 21(2) : 339 -344 . DOI: 10.3724/SP.J.1077.2006.00339

References

1. Poulain M, Poulain M, Lucas J. J. Mater. Res. Bull., 1975, 10: 243--246.
2. 胡和方, 林凤英, 等(HU He-Fang, et al). 硅酸盐学报(Journal of the Chinese Ceramic Society), 1985, 13 (4): 402--407.
3. Hu H, Lin F, Yuan Y, et al. J Master Sci Forum, 1991, 67-78: 239--244.
4.胡和方, 林凤英等. 红外研究, 1987, 6 (2): 137--140.
5. Hu H, Lin F, Yuan Y, \it et al. J Non-Cryst Solids, 1989, 112: 306--308.
6. 曹国喜, 冯际田, 胡和方, 等(CAO Guo-Xi, et al). 硅酸盐崐学报(Journal of the Chinese Ceramic Society), 2003, 31 (1): 52--56.
7. Hurby A. Czech. J. Phys., 1972, 22: 1187.
8. Stanworth J E. Nature, 1952, 169 (4301): 581--582.
9. Stanworth J E. J. Soc. Glass Techno., 1954, 38: 425.
10. 雷宁, 姜中宏, 等(LEI Ning, et al}). 无机材料学报(Journal of Inorganic Materials), 1997, 12 (3): 381--385.
11. Chen Haiyan, Gan Fuxi. J Non-Cryst Solids, 1989, 112: 272--276.
12. Videau J J, Portier J, Priou B. J. Non-Cryst Solids, 1982, 48: 385.
13. Gan F, Jiang Y, Jiang F. Non-Cryst Solids, 1982, 52: 263.
14. Burger H, Kneipp K, Hobert H. Non-Cryst Solids, 1992, 15: 134--142.
15. Sidebottom D L, Hruschka M A, Potter B G.J. NonCryst Solids, 1997, 222: \ 282--289.
16. Zhang J, Qiu J, Yoji K. J. Mater. Lett., 2002, 55: 77--82.
17. Nazabal V, Todoroki S, Nukui A. J. Non-Cryst Solids, 2003, 325: 85--102.
Options
Outlines

/

〈 〉