Effect of Heating Rate on the Morphology of Nano Titanium Dioxide
Received date: 2009-12-21
Revised date: 2010-03-05
Online published: 2010-08-25
Supported by
Nature Science Foundation of Zhejiang Province(Z4080021); National Nature Science Foundation of China(50532030,50625206)
Different shapes of nano titanium dioxide including sphere, rod and irregular-shaped polyhedron were prepared by solvothermal process at heating rates of 240℃/10min, 90℃/10min, 40℃/10min and 20℃/10min using tetrabutyl titanate as Ti source, oleic acid as solvent, dodecylamine as auxiliary agent. TEM, HRTEM and XRD were adopted to characterize the phase composition morphology and phase structure of the final products. The micro-morphology and growth mechanisms of the titanium dioxide nanocrystals prepared at different heating rates were studied based on the TEM, HRTEM and XRD analyses．The results show that spherical, rod-like, and irregular polyhedral points of titanium dioxide nanocrystals could be synthesized by strictly controlling the heating rate. The growth rate of along the (001) direction of nanocrystal shows a first upward and then downward trend with the decline of the heating rate.
LIU Bo, KONG Wei, YE Bo, YU Zhong-Ping, WANG Hua, QIAN Guo-Dong, WANG Zhi-Yu . Effect of Heating Rate on the Morphology of Nano Titanium Dioxide[J]. Journal of Inorganic Materials, 2010 , 25(9) : 906 -910 . DOI: 10.3724/SP.J.1077.2010.00906
[1] Pfaff G, Reynders P. Angle-dependent optical effects deriving from submicron structures of films and pigments. Chem. Rev., 1999, 99(7): 1963-1981.
[2] Lim B C, Thomas N L, Sutherland I. Surface energy measurements of coated titanium dioxide pigment. Pro. Org. Coat., 2008, 62(2): 123-128.
[3] Zallen R, Moret M P. The optical absorption edge of brookite TiO2. Solid State Commun., 2006, 137(3): 154-157.
[4] Thelakkat M, Schmitz C, Schmidt H W. Fully vapor-deposited thin-layer titanium dioxide solar cells. Adv. Mater., 2002, 14(8): 577-581.
[5] 吴聪聪, 卓燕君, 朱沛宁, 等(WU Cong-Cong, et al). 高长径比TiO2纳米管阵列的调控制备及其光阳极性能. 无机材料学报(Journal of Inorganic Materials), 2009, 24(5): 897-901.
[6] Morris D, Egdell R G. Application of V-doped TiO2 as a sensor for detection SO2. J. Mater. Chem., 2001, 11: 3207-3210.
[7] 崔云涛, 王金淑, 李洪义, 等(CUI Yun-Tao, et al). 原位合成TiO2纳米管阵列及其光催化性能研究. 无机材料学报(Journal of Inorganic Materials), 2008, 23(6): 1259-1262.
[8] Jia H M, Zheng Z, Zhao H X, et al. Nonaqueous Sol–Gel synthesis and growth mechanism of single crystalline TiO2 nanorods with high photocatalytic activity. Materials Research Bulletin, 2009, 44(6): 1312-1316.
[9] Manna L, Scher E C, Alivisatos A P. Synthesis of soluble and processable rod-, arrow-, teardrop-, and tetrapod-shaped CdSe nanocrystals. J. Am. Chem. Soc., 2000, 122(51): 12700-12706.
[10] Li Y C, Li X H, Yang C H, et al. Controlled synthesis of CdS nanorods and hexagonal nanocrystals. J. Mater. Chem., 2003, 13: 2641-2648.
[11] Jun Y W, Lee S M, Kang N J, et al. Controlled synthesis of multi-armed CdS nanorod architectures using monosurfactant system. J. Am. Chem. Soc., 2001, 123(21): 5150-5151.
[12] Wang Z, He K Y, He S L, et al. Heating rate dependence of magnetic properties for Fe-based nanocrystalline alloys. Journal of Magnetism and Magnetic Materials, 1997, 171(3): 300-304.
[13] Huo Z Y, Tsung C K, Huang W Y, et al. Self-organized ultrathin oxide nanocrystals. Nano Lett., 2009, 9(3): 1260-1264.
[14] Zhang Z H, Zhong X H, Liu S H, et al. Aminolysis route to monodisperse titania nanorods with tunable aspect ratio. Angew. Chem. Int. Ed., 2005, 117(22): 3532-3536.
[15] Lin J C, Dipre J T, Yates M Z. Microemulsion-directed synthesis of molecular sieve fibers. Chem. Mater., 2003, 15(14): 2764-2773.
[16] Barnard A S, Curtiss L A. Prediction of TiO2 nanoparticle phase and shape transitions controlled by surface chemistry. Nano Lett., 2005, 5(7): 1261-1266.
/
| 〈 |
|
〉 |