SrCo0.4Fe0.4Zr0.2O3-d (SCFZ) mixed conducting hollow fibre membranes were prepared by a dry-wet spinning technology based on the phase separation theory combined with subsequent sintering process. XRD, SEM, thermal expansion technique and oxygen permeation test were utilized to characterize the crystal phase structures, microstructures, sintering behavior and oxygen permeation flux of SCFZ powder and/or hollow fibre membranes. XRD patterns show that the crystal phase of SCFZ hollow fibre membranes are composed of perovskite main phase, SrZrO3 and Co3O4 impurity phases. The content of SrZrO3 increases with increasing the sintering temperature. The SEM images demonstrate that fingerlike pores exist adjacent to the inner and outer skin layer of membrane wall. Meantime, sponge-like pores appear in the middle zone of wall. This kind of morphology is caused by the immersion phase separation process. From the gastight, mechanical strength, sintering behavior, XRD and SEM results, the optimum sintering temperature of the green membranes is considered to be 1240℃. The SCFZ hollow fibre membranes are obtained under the optimum sintering schedule. The sintered SCFZ membranes exhibit high mechanical strength and the fracture strength reaches 74.19MPa. At 850℃, the oxygen permeation flux of the membrane is 2.9´10-7mol/(cm2 · s) under air/He gradient, and the flux is stable during the test for more than 160h.
QI Lü, DONG Xue-Liang, LIU Zhen-Kun, ZHANG Guang-Ru, JIN Wan-Qin . Preparation and Oxygen Permeation of SrCo0.4Fe0.4Zr0.2O3-d Mixed-conducting Hollow Fibre Membrane[J]. Journal of Inorganic Materials, 2010 , 25(8) : 871 -876 . DOI: 10.3724/SP.J.1077.2010.00871
[1]Teraoka Y, Zhang H M, Futukawa S, et al. Oxygen permeation through perovskite-type oxides. Chem. Lett., 1985, 14(11): 1743-1746.
[2]Teraoka Y, Fukada T, Miura N, et al. Preparation of dense film of perovskite-type oxide on porous substrate. J. Ceram. Soc. Jpn. Int. Ed., 1989, 97(5): 533-538.
[3]Jin W Q, Li S G, Huang P, et al. Preparation of an asymmetric perovskite-type membrane and its oxygen permeability.J. Membr. Sci,2001, 185(2):237-243
[4]Okubo T, Haruta K, Kusakabe K, et al. Preparation of a Sol-Gel derived thin membrane on a porous ceramic hollow fiber by the filtration technique.J. Membrane Sci,1991, 59(1):73-80
[5]Luyten J, Buekenhoudt A. Preparation of LaSrCoFeO3-x membranes.Solid State Ionics,2000, 135(1-4):637-642
[6]Tan X Y, Liu Y T, Li K. Preparation of LSCF ceramic hollow-fibre membranes for oxygen production by a phase–inversion/sintering technique.Ind. Eng. Chem. Res,2005, 44(1):61-66
[7]Wang H H, Werth S, Schiestel T, et al. Perovskite hollow-fibre membranes for the production of oxygen-enriched air.Angew. Chem. Int. Ed,2005, 44(42):6906-6909
[8]Wang H H, Werth S, Schiestel T, et al. Simultaneous production of hydrogen and synthesis gas by combining water splitting with partial oxidation of methane in a hollow-fiber membrane reactor.Angew. Chem. Int. Ed,2008, 47(48):9341-9344
[9]Yang L, Tan L, Gu X H, et al. A new series of Sr(Co,Fe,Zr)O3----perovskite-type membrane materials for oxygen permeation. Ind. & Eng. Chem. Res., 2003, 42(11): 2299-2305.
[10]Li S G, Jin W Q, Xu N P, et al. Mechanical strength, and oxygen and electronic transport properties of SrCo0.4Fe0.6O3---YSZ membranes. J. Membr. Sci., 2001, 186(2): 195-204.
[11]Shao Z P, Yang W S, Cong Y, et al. Investigation of the permeation behavior and stability of a Ba0.5Sr0.5Co0.8Fe0.2O3---oxygen membrane. J. Membr. Sci., 2000, 172(1/2): 177-188.
[12]Jin W Q, Zhang C, Zhang P, et al. Thermal decomposition of carbon dioxide coupled with POM in a membrane reactor.AIChE J,2006, 52(7):2545-2550
[13]Takeda Y, Kanno R, Takada T, et al. Phase relation and oxygen- non-stoichiometry of perovskite-like compound SrCoOx (2.29 < x < 2.80). Z. Anorg. Allg. Chem., 1986, 540(9/10): 259-270.
[14]Poulsen F W, van der Puil N . Phase relations and conductivity of Sr- and La-zirconates.Solid State Ionics,1992, 53-56:777-783
[15]Pinnau I, Koros W J. A qualitative skin layer formation mechanism for membrane made by dry/wet phase inversion.J. Polym. Sci., Part B,1993, 31(4):419-427
[16]宁青菊, 谈国强, 史永胜. 无机材料物理性能. 北京: 化学工业出版社, 2005: 74-75.
[17]Schiestel T, Kilgus M, Peter S, et al. Hollow fibre perovskite membranes for oxygen separation.J. Membr. Sci,2005, 258(1/2):1-4
[18]Barbara Z, Wu Z T, Li K. Preparation of ultrathin La0.6Sr0.4Co0.2Fe0.8O3-- hollow fibre membranes for oxygen permeation. Chem. Eng. Sci., 2009, 64(21): 4383-4388.
[19]Chang X F, Zhang C, Dong X L, et al. Effect of sintering atmospheres on sintering behavior, electrical conducivity and oxygen permeability of mixed-conducting membranes.J. Membr. Sci,2008, 316(1/2):128-136
/
〈 |
|
〉 |