Research Paper

Fabrication and Anticorrosion Property of Superhydrophobic Surfaces with Hierarchical Structure through an Organic-inorganic Self-assemble Process

Expand
  • (College of Material Science and Technology, Nanjing University of Aeronautics and Astronautics, Nanjing 210016, China)

Received date: 2009-11-16

  Revised date: 2010-01-21

  Online published: 2010-06-10

Abstract

A superhydrophobic surface was obtained by using g-aminopropyltriethoxylsilane (KH550) as a linker from organic-inorganic self-assemble process. By utilizing silane with amine functional group and Si-hydroxy functional group, bionic superhydrophobic surfaces with hierarchical microsphere/nanofiber structures were prepared on metal surfaces. The corrosion behavior of the composite film was investigated by electrochemicial impedance spectroscope (EIS). The maximal contact angle for water on the composite film is about 152°. Scanning electron microscope (SEM). Test result shows that the lotus-like film has microsphere/nanofiber hierarchical structure. The surface of the film forms a composite framework which plays an essential role in trapping air between the solid substrate and the liquid droplets to get high contact angle and low roll angle. Electrochemical corrosion measurements results indicate that the composite film has excellent corrosion protection for mild steel. The corrosion current of mild steel is nearly 1´104 times than that of the sample coated with the composite film, while the corrosion impedance increases dramatically. It suggests that the superdrophobic film has good corrosion resistance.

Cite this article

DI Zhi-Yong, HE Jian-Ping, ZHOU Jian-Hua, SUN Dun, WANG Tao . Fabrication and Anticorrosion Property of Superhydrophobic Surfaces with Hierarchical Structure through an Organic-inorganic Self-assemble Process[J]. Journal of Inorganic Materials, 2010 , 25(7) : 765 -769 . DOI: 10.3724/SP.J.1077.2010.00765

References

[1]Nakajima A, Saiki C, Hashimoto K, et al. Processing of roughened silica film by colloidal silica for super-hydrophobic coating. J. Mater. Sci. Lett., 2001, 20(21): 1975-1977.
[2]Pilotek S, Schmidt H K. Wettability of microstructured hydrophobic Sol-Gel coatings. Journal of Sol-Gel and Technology, 2003, 26(1): 789-792.
[3]Shirtcliffe N J, McHale G, Newton M I, et al. Wetting and wetting transitions on copper-based super-hydrophobic surfaces. Langmuir, 2005, 21(3): 937-943.
[4]Wu Y, Bekke M, Moue Y, et al. Mechanical durability of ultrawater-repellent thin film with microwave plasma-enhanced CVD. Thin Solid Films, 2004, 457(1): 122-127.
[5]Liu H, Feng L, Zhai J, et al. Reversible wettability of a chemical vapor deposition prepared ZnO film between superhydrophobicity and superhydrophilicity. Langmuir, 2004, 20(14): 5659-5661.
[6]Erbil Y H, Demirei A L, Avci Y, et al. Transformation of a simple plastic into a superhydrophobic surface. Science, 2003, 299(5611): 1377-1380.
[7]Song X, Zhai J, Wang Y, et al. Fabrication of superhydrophobic surfaces by self-assembly and their water-adhesion properties. J. Phys. Chem. B, 2005, 109(9): 4048-4052.
[8]Jung D H, Park I J, Choi Y K, et al. Perfluorinated polymer monolayers on porous silica for materials with super liquid repellentp roperties. Langmuir, 2002, 18(16): 6133-6139.
[9]Tadanaga K, Kitamuro K, Matsuda A, et al. Formation of superhydrophobic alumina coating films with high transparency on polymer substrates by the Sol-Gel method. Journal of Sol-Gel and Technology, 2003, 26(1): 705-708.
[10]Shang H M, Wang Y, Limmer S J, et al. Optically transparent superhydrophobic silica-based films. Thin Solid Films, 2005, 472(1): 37-43.
[11]Nakajima A, Abe K, Hashimoto K, et al. Preparation of hardsuper-hydrophobic films with visible light transmission. Thin Solid Films, 2000, 376(1): 140-143.
[12]Barthlott W, Neinhuis C. Purity of the sacred lotus, or escape from contamination in biological surfaces.Plant,1997, 202(1):1-8
[13]Kock K, Bhushan B, Jung Y C, et al. Fabrication of artificial lotus leaves and significance of hierarchical structure for superhydrophobicity and low adhesion. Soft Matter, 2009, 5: 1386-1393
[14]翟 锦, 李欢军, 李英顺, 等(ZHAI Jin, et al). 碳纳米管阵列超双疏性质的发现. 物理(Physics), 2002, 31(8): 483-485.
[15]Cassie A B D, Baxter S. Large contact angles of plant and animal surfaces. Nature, 1945, 155: 21-22.
[16]Luo Z Z, Zhang Z Z, Hu L T, et al. Stable bionic superhydrophobic coating surface fabricated by a conventional curing process. Advanced Materials, 2008, 20(5): 970-974.
[17]Michele M, Alessandro C, Luisa D M, et al. Durable superhydrophobic and antireflective surfaces by trimethylsilanized silica nanoparticles-based Sol-Gel processing. Langmuir, 2009, 25(11): 6357-6362.
[18]曹楚南, 张鉴清. 电化学阻抗谱导论. 北京: 科学出版社, 2002: 20-36.

Outlines

/