Adv. Search
Journal of Inorganic Materials

Journal of Inorganic Materials >

2010 , Vol. 25 >Issue 4: 406 - 410

DOI: https://doi.org/10.3724/SP.J.1077.2010.00406

Research Paper

Synthesis and Microwave Absorbing Properties of FeCoNi Alloy Particles/Graphite Flaky Composites

  • WANG Chen ,
  • KANG Fei-Yu ,
  • GU Jia-Lin
Expand
  • Laboratory of Advanced Materials, Department of Materials Science and Engineering, Tsinghua University, Beijing 100084, China

Received date: 2009-07-23

  Revised date: 2009-09-13

  Online published: 2010-04-27

Fold

Abstract

Exfoliated graphite was separated into nanosized flakes by ultrasonication and acid treatment, and then FeCoNi alloy particles were deposited uniformly on the surface of flakes by codeposition method and annealing treatment process. Magnetic and microwave absorbing properties of the obtained samples were measured. The results show that the synthesized composites possess good soft magnetic performance and effective microwave absorption. The composite consisting of Fe3Co6Ni/graphite flakes annealed at 600℃ as an absorber has the maximum absorption value of -24dB at 12.6GHz, and the effective absorbing bandwidth (<-5dB) is about 8GHz. The characteristics of microwave absorption can be controlled by adjusting element ratios in alloy and the parameters of heat treatment process. This kind of composite has great potential and investigation value in microwave absorbing fields.

Key words： graphite flakes; FeCoNi alloy; microwave absorbing materials

Cite this article

WANG Chen , KANG Fei-Yu , GU Jia-Lin . Synthesis and Microwave Absorbing Properties of FeCoNi Alloy Particles/Graphite Flaky Composites
[J]. Journal of Inorganic Materials, 2010 , 25(4) : 406 -410 . DOI: 10.3724/SP.J.1077.2010.00406

References

[1］Li D, Kaner R B. Graphenebased materials. Science, 2008, 320(5880): 1170-1171.
［2］Westervelt R M. Graphene nanoelectronics. Science, 2008, 320(5874): 324-325.
［3］贾宝富, 刘述章, 林为干. 反雷达涂敷材料中吸收粒子的最佳外形. 电子科技大学学报, 1990, 19(4)：342-345.
［4］彭俊芳. 填充磁性微粒的石墨基复合材料的电磁性能研究. 北京: 清华大学硕士论文, 2002.
［5］屈战民. 用于电磁屏蔽与吸收材料的镀镍石墨粉的研究. 电镀与环保, 2007, 27(4)：29-31.
［6］汪桃生, 吴大军, 吴翠玲, 等. 纳米石墨基导电复合涂料的电磁屏蔽性能. 华侨大学学报(自然科学版), 2007, 28(3)：278-281.
［7］周明善, 李澄俊, 徐 铭, 等(ZHOU Ming-Shan, et al). 膨胀石墨复合材料的电磁特性及其3mm、8mm波动态衰减性能研究. 无机材料学报(Journal of Inorganic Materials), 2007, 22(3)：509-513.
［8］Lee S E, Choi O, Hahn H T. Microwave properties of graphite nanoplatelet/epoxy composites. J. Appl. Phys., 2008, 104(3): 0037051-7.
［9］Fan Y Z, Yang H B, Liu X Z, et al. Preparation and study on radar absorbing materials of nickelcoated carbon fiber and flake graphite. J. Alloy. Compd., 2008, 461(1/2): 490-494.
［10］Yang L, Huan H, Liu H B, et al. Preparation and microwave absorption properties of FeNi/graphite nanocomposites. Trans. Nonferrous Met. Soc. China, 2007(17): S708-S712.
［11］Liu H B, Zou Y H, Yang L, et al. The influence of temperature on magnetic and microwave absorption properties of Fe/graphite oxide nanocomposites. J. Magn. Magn. Mater., 2006, 302(2): 343-347.
Options
Outlines

/

〈 〉