Journal of Inorganic Materials

Journal of Inorganic Materials >

2010 , Vol. 15 >Issue 2: 163 - 167

DOI: https://doi.org/10.3724/SP.J.1077.2010.00163

Research Paper

Preparation of Trimodal Macro-meso-microporous Aluminosilicates by Colloidal Crystal/P123 Dual Templates

  • SONG Wei-Juan ,
  • LIU Hong-Tao ,
  • WANG Kun ,
  • CAO Jin ,
  • XU Chun-Yan ,
  • ZHANG Ze-Ting
Expand

  • (1. State Key Laboratory of Chemical Resource Engineering, Beijing University of Chemical Technology, Beijing 100029, China; 2. East China Lube Sales Company, PetroChina Company Limited, Shanghai 200122, China)

Received date: 2009-03-23

  Revised date: 2009-09-14

  Online published: 2010-02-20

Fold

Abstract

Polystyrene (PS) microspheres with average diameter of 50nm and 450nm were prepared by step emulsion polymerization and emulsifier-free emulsion polymerization, respectively. On the basis of this, aluminosilicates with macro-meso-micropores were synthesized via insitu assembly of Y zeolite precursors by PS microspheres/P123 dual templates. The materials with macro-meso-micropores were characterized by means of XRD, SEM and TEM. The results showed that PS microspheres with the diameter of 50nm and 450nm can be obtained by step emulsion polymerization and emulsifier-free emulsion polymerization, respestively. Moreover, influence of various factors including diameters of PS microspheres, amount of templates, and amount of water on the synthesis of the macro-meso-microporous materials were systematically investigated. It was concluded that the composites synthesized by PS microspheres with the larger diameter contained more dispersed macropores. The optimum conditions for aluminosilicates preparation were found to be PS/precursors ratio of 1-0.5, water/precursors ratio of 7.5, and P123/precursors ratio of 0.1.

Key words： macro-meso-microporous aluminosilicates; colloidal crystal; block copolymer; assembly; characterization

Cite this article

SONG Wei-Juan , LIU Hong-Tao , WANG Kun , CAO Jin , XU Chun-Yan , ZHANG Ze-Ting . Preparation of Trimodal Macro-meso-microporous Aluminosilicates by Colloidal Crystal/P123 Dual Templates[J]. Journal of Inorganic Materials, 2010 , 15(2) : 163 -167 . DOI: 10.3724/SP.J.1077.2010.00163

References

［1］李学平, 陈爱忠. FCC催化剂现状及其发展方向. 工业催化, 2003, 11(8): 21-23.

［2］Tan Q, Bao X, Song T, et al. Synthesis, characterization, and catalytic properties of hydrothermally stable macro-meso-micro-porous composite materials synthesized via in situ assembly of zeolite Y nanoclusters on kaolin. Journal of Catalysis, 2007, 251(1): 69-79.

［3］Tan Q, Fan Y, Liu H, et al. Bimodal micro-meso-porous aluminosilicates for heavy oil cracking: Pore structure tuning and catalytic properties. AIChE Journal, 2008, 54(7): 1850-1859.

［4］Ikari K, Suzuki K, Imai H. Grain size control of mesoporous silica and formation of bimodal pore structure. Langmuir, 2004, 20(26): 11504-11508.

［5］Sel O, Kuang D, Thommes M, et al. Principles of hierarchical meso- and macropore architectures by liquid crystalline and polymer colloid templating. Langmuir, 2006, 22(5): 2311-2322.

［6］Zhang F Q, Yan Y, Meng Y, et al. Ordered bimodal mesoporous silica with tunable pore structure and morphology. Microporous and Mesoporous Materials, 2007, 98(1/2/3): 6-15.

［7］Wan Y, Zhao D. On the controllable soft-templating approach to mesoporous silicates. Chemical Reviews, 2007, 107(7): 2821-2860.

［8］Zhang Z, Han Y, Xiao F, et al. Mesoporous aluminosilicates with ordered hexagonal structure, strong acidity, and extraordinary hydrothermal stability at high temperatures. Journal of the American Chemical Society, 2001, 123(21): 5015-5021.

［9］Han Y, Li D, Zhao L, et al. High-temperature generalized synthesis of stable ordered mesoporous silica-based materials by using fluorocarbonhydrocarbon surfactant mixtures. Angew. Chem. Int. Ed Engl., 2003, 42(31): 3633-3637.

［10］宋春霞, 杨立新, 陈小明,等(SONG Chun-Xia, et al). 胶晶模板法制备3DOM尖晶石型LiMn2O4及表征. 高等学校化学学报(Chemical Journal of Chinese Universities), 2007, 28(2): 204-207.

［11］Tang F, Uchikoshi T, Sakka Y. A practical technique for the fabrication of highly ordered macroporous structures of inorganic oxides. Materials Research Bulletin, 2006, 41(2): 268-273.

［12］Lee S G, Jang Y S, Park S S. Synthesis of fine sodium-free silica powder from sodium silicate using w/o emulsion. Materials Chemistry and Physics, 2006, 100(2/3): 503-506.

［13］张 凯, 傅 强, 黄渝鸿. 聚苯乙烯单分散微球粒径可控性探讨. 离子交换与吸附, 2006, 22(2): 140-145.

［14］崔 匀, 刘洪涛, 金君素, 等. 炭黑/P123双重模板体系原位组装梯度孔材料. 化工学报, 2008, 59(10): 2668-2675.

Options
Outlines

/

〈 〉