SiCn/SiC Multilayer Oxidation Protective Coatings for C/C Composites
Prepared by a Hydrothermal Electrophoretic Deposition Process

  • LIU Miao ,
  • HUANG Jian-Feng ,
  • WANG Bo ,
  • CAO Li-Yun ,
  • WU Jian-Peng
Expand
  • (Key Laboratory of Auxiliary Chemistry and Technology for Chemical Industry, Ministry of Education, Shaanxi University of Science and Technology, Xi’an 710021, China)

Received date: 2009-03-16

  Revised date: 2009-05-14

  Online published: 2010-04-22

Fold

Abstract

Nano-SiC coatings (SiCn) were deposited on SiC-C/C composites surface by a hydrothermal electrophoretic deposition. Phase compositions, surface and cross-section morphologies of the as-prepared multilayer coatings were characterized by XRD and SEM. The influences of hydrothermal deposition temperatures on the microstructures and high temperature oxidation resistance of the SiCn coatings were particularly investigated. And the invalidation behaviors of the as-prepared multilayer coatings coated samples at 1600℃ were analyzed. Results show that the as-prepared nano-SiC outer layers are composed of β-SiC. The thickness and density of the nano-SiC coatings improve with the increase of hydrothermal temperature. With the increase of hydrothermal temperature, the anti-oxidation properties of the coating samples increase. The prepared coating samples deposited at 120℃ can effectively protect C/C composites from oxidation at 1500℃ in air for 202h with weight loss only about 2.16×10-3g/cm2. While the weight loss of coated C/C composites after 64h oxidation at 1600℃ in air is 3.7×10-3g/cm2. The failure of the coatings is due to the long time volatilization of SiO2 thin film at high temperature, which makes the coating defects fail to be self-cured by SiO2 glass layer and form the penetrative microholes in the SiC bonding layer.

Key words： C/C composites; nano-SiC; hydrothermal electrophoretic deposition

Cite this article

LIU Miao , HUANG Jian-Feng , WANG Bo , CAO Li-Yun , WU Jian-Peng . SiCn/SiC Multilayer Oxidation Protective Coatings for C/C Composites
Prepared by a Hydrothermal Electrophoretic Deposition Process[J]. Journal of Inorganic Materials, 2009 , 24(6) : 1214 -1218 . DOI: 10.3724/SP.J.1077.2009.01214

References

［1］Buckley J D. Am. Ceram. Soc. Bull., 1988, 67(2): 364-368.
［2］Sheehan J E, Buesking K W, Sullivan B J. Annu. Rev. Mater. Sci., 1994, 24: 19-44.
［3］Westwood M E, Webster J D, Day R J, et al. J. Mater. Sci., 1996, 31(6): 1389-1397.
［4］黄剑锋, 李贺军, 熊信柏, 等. 新型炭材料, 2005, 20(4): 1-7.
［5］Jacobson N S, Curry D M. Carbon, 2006, 44(7): 1142-1150.
［6］Huang J F, Li H J, Zeng X R, et al. Surf. Coat. Technol., 2006, 200(18/19): 5379-5385.
［7］Li H J, Fu Q G, Shi X H, et al. Carbon, 2006, 44(3): 602-605.
［8］曾燮榕, 杨 峥, 李贺军, 等. 航空材料学报, 1997, 18(4): 427-431.
［9］Huang M, Li K Z, Li H J, et al. Carbon, 2007, 45(5): 1124-1126.
［10］Zheng G B, Mizuki H, Sano H, et al. Carbon, 2008, 46(13): 1808-1811.
［11］Huang J F, Zeng X R, Li H J, et al. Carbon, 2003, 41(14): 2825-2829.
［12］曾燮榕, 李贺军, 张建国, 等. 复合材料学报, 2000, 17(2): 42-45.
Options
Outlines

/

〈 〉