Rutile titanium oxide films on silicon substrate were prepared by unbalanced reactive pulsed magnetron sputtering and subsequently modified by hydrogen plasma reduction. The XRD patterns show that the modified titanium oxide films consist of single rutile phase, which is similar to as-deposited films. FTIR results exhibit that no obvious -OH groups exist in the films. XPS spectra display that oxygen deficiency exist in the film after hydrogen plasma reduction. The wettability experiment show that the hydrophilicity of the hydrogen plasma modified Ti-O films decreases slightly. The anticoagulation property of Ti-O films modified at lower temperature in short time (110℃, 15min) is obviously improved, which is related to the content of oxygen deficiency. Consequently hydrogen introducing is an effective way to improve the anticoagulation property of titanium oxide films.
XU Yi
,
HUANG Nan
,
SUN Hong
. Blood Compatibility of Titanium Oxide Films Modified by Hydrogen Plasma Reduction[J]. Journal of Inorganic Materials, 2008
, 23(6)
: 1246
-1252
.
DOI: 10.3724/SP.J.1077.2008.01246
[1] Huang N, Yang P, Cheng X, et al. Biomaterials, 1998, 19 (7-9): 771-776.
[2] Feng L, Andrade D J. J. Coll. Interf. Sci., 1994, 166 (2): 419-426.
[3] Huang N, Yang P, Leng Y X, et al. Biomaterials, 2003, 24 (13): 2177-2187.
[4] Yang P, Huang N, Leng Y X, et al. Surface & Coatings Technology, 2002, 156 (1-3): 284-288.
[5] Liu H, Ma H T, Li X Z, et al. Chemosphere, 2003, 50 (1): 39-46.
[6] 杨萍, 曾晓兰, 黄楠, 等. 西南交通大学学报, 1998, 33 (2): 183-187.
[7] 张前程, 张凤宝, 张国亮, 等. 燃料化学学报, 2004, 32 (2): 240-243.
[8] Huang Aimin, Cao Lixin, Chen Jie, et al. Journal of Catalysis, 1999, 188 (1): 40-47.
[9] Ivandaa M, Music S, Popovic S, et al. Journal of Molecular Structure, 1999, 480-481: 645-649.
[10] 王春仁. 国外医学生物医学工程分册, 1995, 18 (6): 334-337.
[11] 王传华, 冷希岗. 国外医学生物医学工程分册, 1998, 21 (1): 1-5.
[12] Sharma P K, Hanumantha Rao K. Advances in Colloid and Interface Science, 2002, 98 (3): 341-463.
[13] 程青, 王国斌. 上海生物医学工程杂志, 2001, 22 (3): 31-33.
[14] 胡国栋. 国外医学生物医学工程分册, 2002, 25 (6): 271-273.
[15] Lee J, Lee H. Journal of Biomedical Materials Research, 1998, 41 (2): 304-311.