Advanced silicon nitride ceramics with high wear resistance were fabricated by colloidal process. Orthogonal design was utilized to optimize the process parameters.The change of Zeta potential for Si3N4 particles after adding dispersant was analyzed. Furthermore, the microstructure, mechanical properties and wear resistance of silicon nitride ceramics were investigated. The results indicate that the green body with high density can be formed when the volume fraction of solid phase of silicon nitride slurry is equal to 45%. And silicon nitride ceramics with fracture toughness of 7.21MPa·m1/2, hardness of 9.30GPa is obtained in the optimum condition. The friction and wear tests show that silicon nitride ceramics happen to crisp rupture and break off in the dry condition; while in the water-lubricated condition, the film of Si(OH)4 is formed on the friction surface, and the wear mechanism is mainly chemical fretting wear.
HAO Hong-Shun
,
XU Li-Hua
,
ZHANG Xiao-Meng
,
LIU Ming
,
FU Zhi
. Preparation of Silicon Nitride Ceramics with High Wear Resistance by Aqueous Colloidal Process[J]. Journal of Inorganic Materials, 2008
, 23(5)
: 955
-959
.
DOI: 10.3724/SP.J.1077.2008.00955
[1] 陈福山, 杜大明, 宋士华. 佛山陶瓷, 2005, (11): 1--4.
[2] 刘学建, 黄莉萍, 古宏晨, 等(LIU Xue-Jian, et al). 无机材料学报(Journal of Inorganic Materials), 2001, 16 (5): 877--882.
[3] Xu Lihua, Lian Fang, Xia Wen, et al. Journal of Basic Science and Engineering, 2004, 12 (2): 179--186.
[4] 石维佳, 王宗英, 张而耕, 等. 润滑与密封, 2000, (4): 39--41.
[5] 斯松华, 方亮, 高义民, 等. 摩擦学学报, 1997, 17 (1): 32--37.
[6] 任靖日, 李花, 金石三. 延边大学学报(自然科学版), 2003, 29 (3): 212--215.
[7] Hsu S M, Shen Ming. Wear, 2004, 256: 867--878.
[8] 闫玉涛, 李保民, 王丹. 润滑与密封, 2005, (4): 75--76.
[9] Gomes J R, Miranda A S, Vieira J M, et al. Wear, 2001, 250: 293--298.
[10] 徐利华, 刘明, 夏雯, 等. 胶态成型制备氮化硅耐磨陶瓷的方法. 中国 ZL200410009294.0.2006-06-21.
[11] 南京化工学院编. 陶瓷物理化学. 北京: 中国建筑工业出版社, 1981.
[12] Cesarano J, Aksay I A. J. Am. Ceram. Soc., 1988, 71 (12): 1062--1067.
[13] 扶志. 胶态成型工艺制备精细耐磨陶瓷的研究. 北京科技大学硕士学位论文, 2003.
[14] 刘明, 徐利华, 夏雯, 等. 稀有金属材料与工程, 2005, 34 (suppl.1): 359--362.
[15] 赵世海, 杨正方. 润滑与密封, 2005, (5): 199--202.
[16] Zhao Xingzhong, Liu Jiajun, Zhu Baoliang, et al. Ceramics International, 1999, 25: 309--315.
[17] Tanita Y, Mine T, Nakajima K. J. Tribology, 1990, 112: 637--642.
[18] Ishigaki H, Kawaguchi I, Twasa M. Wear, 1988, 121: 107--116.