The ultraviolet light photosensitive Ba0.8Sr0.2TiO3 (BST) sol and gel films were prepared by using chemical modification and modified sol-gel process with polyvinylpyrrolidone (PVP) as crack-suppressing agent, and acetylacetone (AcAcH) as chemical modifier agent which can associate metal-salt to form coordination chelate. The BST patterned gel films were prepared by irect patterning process. Then the BST patterned films with perovskite structure on Pt/TiO2/SiO2/Si substrate were obtained after subsequent heat treatment. The thickness of the BST patterned film is about 793nm, the dielectric constant and dielectric loss of the BST patterned film are about 600 and 0.03, respectively.
ZHANG Wei-Hua
,
YUAN Yuan
,
SHI Chun-Mei
,
ZHAO Gao-Yang
. BST Patterned Films Prepared by Direct Patterning Process and Their Properties[J]. Journal of Inorganic Materials, 2008
, 23(5)
: 886
-890
.
DOI: 10.3724/SP.J.1077.2008.00886
[1] 朱小红, 朱建国, 郑东宁, 等(ZHAU Xiao-Hong, et al). 无机材料学报(Journal of Inorganic Materials), 2003, 18 (5): 989-997.
[2] 陈宏伟, 杨传仁, 符春林, 等. 功能材料, 2004, 35 (5): 615--617.
[3] Ramesh R, Aggarwal S, Auciello O. Materials Science and Engineering, 2001, 32 (6): 191--236.
[4] 包定华, 张良莹, 姚熹. 硅酸盐通报, 1998, 3 (3): 59--63.
[5] Tohge N, Takama Y. Journal of Materials Science: Materials in Electonic, 1999, 10 (4): 273--277.
[6] Alexe M, Harnagea C, Hesse D. Journal of Electroceramics, 2004, 12 (1): 69--88.
[7] 张卫华, 赵高扬, 李莺, 等. 半导体学报, 2006, 27 (9): 1590--1594.
[8] Xinghua P, Weigen L, Aili D, et al. Materials Research Bulletin, 2001, 36 (7): 1471--1478.
[9] Zheyao W, Jianshe L, Tianling R, et al. Sensors and Actuators, 2005, 117 (2): 293--300.
[10] 杨文, 常爱民, 庄建文, 等(YANG Wen, et al). 无机材料学报(Journal of Inorganic Materials), 2004, 12 (1): 69--88.
[11] 叶杨, 丁爱丽, 唐新桂, 等(YE Yang, et al). 无机材料学报(Journal of Inorganic Materials), 2002, 17 (1): 125-130.