Influence of modulating ratio on friction and wear behavior of TiN/Ti multilayer coatings was studied. Filtered cathode vacuum arc(FCVA) deposition method was applied in preparation of TiN/Ti multilayer coatings with different modulating ratios. Scanning electron microscope (SEM) and transmission electron microscope (TEM) were used in the film structure observation and individual layer analysis. Furthermore, nanohardness and elastic module were tested by nano-indenter and the friction and wear experiment was carried out on SRV tester. The experimental results show clear laminate structures in TiN/Ti multilayer coatings and good bonding between film and substrate. Nanohardness and the wear behavior are influenced remarkably by modulating ratio. Influence of modulating ratio on friction of multilayer coatings is relatively weak. Finally, the relationship between the ratio of hardness and elastic module (H/E) and the wear behavior of TiN/Ti multilayer coatings is discussed.
GONG Hai-Fei
,
SHAO Tian-Min
,
ZHANG Chen-Hui
,
XU Jun
. Influence of Modulating Ratio on Friction and Wear Behavior of TiN/Ti Multilayer Coatings[J]. Journal of Inorganic Materials, 2008
, 23(4)
: 758
-762
.
DOI: 10.3724/SP.J.1077.2008.00758
[1] 于翔, 王成彪, 刘阳, 等. 金属学报, 2006, 42 (6): 662--666.
[2] 刘元富, 张谷令, 王久丽, 等. 物理学报, 2004, 53 (2): 503--507.
[3] Holleck H, Schier V. Surface and Coatings Technology, 1995, 76-77: 328--336.
[4] Bull S J, Jones A M. Surface and Coatings Technology, 1996, 78: 173--184.
[5] 李谋, 李晓娜, 林国强, 等. 材料热处理学报, 2005, 26: 49--52.
[6] 李戈扬, 施晓蓉, 张流强, 等. 上海交通大学学报, 1999, 33 (2): 159--161.
[7] 赖倩茜, 虞晓江, 戴嘉维, 等. 真空科学与技术, 2002, 22 (4): 313--316.
[8] Dheepa Srinivasana, Trupti G Kulkarnib, Anand K. Tribology International, 2007, 40 (2): 266--277.
[9] 赵彦辉, 林国强, 李晓娜, 等. 金属学报, 2005, 41 (10): 1106--1110.
[10] Voevodin A A, Iarve E V, Ragland W, et al. Surface and Coatings Technology, 2001, 148: 38--45.
[11] 刘成龙, 林国强, 杨大智, 等(LIU Cheng-Liong, et al). 无机材料学报(Journal of Inorganic Materials), 2005, 20 (4): 940--946.
[12] Simmonds M C, van Swygenhovena H, Pfliigerb E, et al. Surface and Coatings Technology, 1997, 94-95: 490--494.
[13] Mats Larsson, Michael Bromark, Per Hedenqvist, et al. Surface and Coatings Technology, 1995, 76-77: 202--205.
[14] 赵阳, 王娟, 徐晓明, 等. 金属学报, 2006, 42 (4): 389--393.
[15] Ghosha S K, Limayeb P K, Swainc P B, et al. Surface and Coatings Technology, 2007, 201: 4609--4618.
[16] Lewis D B, Donohue L A, Lembke M, et al. Surface and Coatings Technology, 1999, 114: 187--199.
[17] Leyland A, Matthews A. Wear, 2000, 246: 1--11.
[18] Leyland A, Matthews A. Surface and Coatings Technology, 2004, 177-178: 317--324.