Porous Si3N4 ceramics were prepared by in situ reaction-bonding technology, using Si3N4 and Al2O3 as starting materials. The effects of sintering temperature and holding time on their porosities, flexural strength, and dielectric properties were studied. The strength and dielectric constants of samples are improved with increasing of sintering temperature and holding time; but the result is reverse in the condition of sintering temperature >1350℃ and holding time >4h. The phase analyses results indicate that the porous Si3N4 ceramics are mainly composed of α-Si3N4, oxidated SiO2 (cristobalite) and Al2O3. Porous Si3N4 ceramics with porosities from 25.34% to 43.92% and flexural strength from 42.54 to 127.85MPa are obtained. Their dielectric constants are in the range from 3.3 to 4.6 and dielectric loss is about 0.005.
XIA Yong-Feng
,
ZENG Yu-Ping
,
JIANG Dong-Liang
. Preparation and Dielectric Properties of In Situ Reaction Bonded Porous Si3N4 Ceramics[J]. Journal of Inorganic Materials, 2008
, 23(4)
: 705
-709
.
DOI: 10.3724/SP.J.1077.2008.00705
[1] 闫联生, 李贺军, 崔 红. 宇航材料工艺, 2004, 2: 14-16.
[2] 张大海, 黎 义, 高 文, 等. 宇航材料工艺, 2001, 6: 1-3.
[3] Zhu X W, Zhou Y, Hirao K. J. Am. Ceram. Soc., 2006, 89 (11): 3331-3339.
[4] Jung I C, Sun H C, Sang W N, et al. Materials letters, 2007, 61 (26): 4843-4846.
[5] Fukasawa T, Deng Z Y, Ando M. J. Am. Ceram. Soc., 2002, 85 (9): 2151-2155.
[6] Diaz A, Hampshire S. J. Eur. Ceram. Soc., 2004, 24 (2): 413-419.
[7] Yang J F, Ohji T, Niihara K. J. Am. Ceram. Soc., 2000, 83 (8): 2094-2096.
[8] Kawal C. J. Mater. Sci., 2001, 36 (24): 5713-5717.
[9] Yang J F, Deng Z Y, Ohji T. J. Eur. Ceram. Soc., 2003, 23 (2): 371-378.
[10] Chen F, Shen Q, Yan F Q, et al. J. Am. Ceram. Soc., 2007, 90 (8): 2379-2383.
[11] Ding S Q, Zeng Y P, Jiang D L. Materials Letters, 2006, 61 (11-12): 2277-2280.
[12] 姚俊杰, 李包顺, 黄校先, 等. 功能材料与器件学报, 1996, 2 (2): 65-70.
[13] Meyer F P. Proceedings the l5th Symposium on Electromagnetic Windows, Georgia Institute of Technology, Atlanta, Georgiat. 1980. 170-178.
[14] 朱新文, 江东亮, 谭寿洪. 中国粉体技术, 2000, 6 (5): 118-211.
[15] 张其士, 李旭平. 耐火材料, 1997, 31 (5): 256-259, 262.
[16] 关振铎, 张中太, 焦金生. 无机材料物理性能. 第1版. 北京: 清华大学出版社, 2004. 315-316.
[17] Mruthyunjaya L, Raokns. Spacer Technol., 1996, 6 (2): 28-31.
[18] Thorp J S, Ahmad A B, Kulesza B L J, et al. J. Mater. Sci., 1984, 19 (10): 3211-3216.
[19] Penn S J, Alford N M, Templeton A, et al. J. Am. Ceram. Soc., 1997, 80 (7): 1885-1888.