Preparation and Properties of Carbon Fiber Needling Preform Reinforced Silicon Carbide Composites

  • YAN Lian-Sheng ,
  • CUI Hong ,
  • LI Ke-Zhi ,
  • LI He-Jun ,
  • WANG Tao ,
  • Song Mai-Li
Expand
  • 1. Material Department, Northwestern Polytechnical University,
    Xi’an 710072, China; 2. Xi’an Aerospace Composite Material Institute, Xi’an 710025, China

Received date: 2007-03-14

  Revised date: 2007-06-02

  Online published: 2008-03-20

Abstract

Carbon fiber needling preform
reinforced C/SiC composites were prepared by “CVI+PIP”combined process.
The densification efficiency, the microstructure and properties of the C/SiC
composites reinforced by carbon fiber needling preform were investigated
compared with 3D woven preform and pre-oxidation PAN fiber needling preform reinforced C/SiC composites. The results show that the densification
efficiency of carbon fiber needling preform is higher than that of 3D
woven preform. Under the same densification processing condition, the densitis of the composites reinforced with carbon fiber needling preform and pre-oxidation PAN fiber needling preform reach 2.08g/cm3 and 2.02g/cm3, respectively, while the density of the composites reinforced with 3D woven preform is merely 1.81g/cm3. The composites reinforced with carbon fiber needling perform exhibits good mechanical properties with flexural strength of 237MPa and shear strength of 26MPa, respectively.

Cite this article

YAN Lian-Sheng , CUI Hong , LI Ke-Zhi , LI He-Jun , WANG Tao , Song Mai-Li . Preparation and Properties of Carbon Fiber Needling Preform Reinforced Silicon Carbide Composites[J]. Journal of Inorganic Materials, 2008 , 23(2) : 223 -228 . DOI: 10.3724/SP.J.1077.2008.00223

References

[1] Naslain R. High Temperature Ceramic Matrix Composite, London: Woodhead Publications, 1993. 735--778.
[2] Nannetti C A, Riccardi B, Ortona A. Journal of Nuclear Materials, 2002, 307-311 (2): 1196--1199.
[3] 张立同, 成来飞, 徐永东. 航空制造技术, 2003, (1): 24--32.
[4] 闫联生, 邹武. 固体火箭技术, 1998, 21 (1): 54--58.
[5] Zheng G B, Sano H, Uchiyama Y, et al. J. Mater. Sci., 1999, 34 (4): 827--834.
[6] 闫联生, 王涛, 邹武, 等. 宇航材
料工艺, 1999, 29 (3): 38--41.
[7] Lackey J, Hanigofsky J A, Freeman G B, et al. J. Am. Ceram. Soc., 1995, 78 (6): 1564--1570.
[8] Inghels E, Lamon J. J. Mater. Sci., 1991, 26 (11): 5403--5410.
[9] Kaya H. Journal of Composite Science & Technology, 1999, 59 (3): 861--872.
[10] Trabandt U, Wulz H G, Schmid T. Journal of Key Engineering Materials, 1999, 164-165 (2): 445--450.
[11] Loumagne F, Langlais F, Naslain R, et al. Thin Solid Films, 1995, 254 (1): 75--82.
[12] 尹洪峰, 徐永东, 成来飞, 等(YIN Hong-Feng, et al). 硅酸盐学报(Journal of The Chinese Ceramic Society), 2000, 28 (5): 437--440.
Outlines

/