A SiC-WSi2/MoSi2 multilayer oxidation protective coating for carbon/carbon (C/C) composites was prepared by pack cementation. Effects of the total content of W and Mo on the microstructure and high temperature anti-oxidation property of the multi-coating were studied by XRD, SEM, EDS and isothermal oxidation test. The results show that with the total content of W and Mo increasing in the pack powders, the as-received multi-coating thickness first increases and then decreases. The multi-coating with 10.0at％ (W and Mo) has a thicker, denser structure and higher content of WSi2 and
MoSi2 than those with 0at％, 8.4at％ and 13.1at％ (W and Mo). A stable and dense glassy SiO2 film can be formed on the coating surface with 10.0at％
(W and Mo) during the oxidation test. The coated specimen with 10.0at％ (W and Mo) has no weight loss after oxidation in air for 315h at 1500℃ and no cracks after thermal cycling between 1500℃ and room temperature for 18 times, which implies that the multicoating has excellent oxidation protective ability and thermal shock resistance.
HOU Dang-She
,
LI Ke-Zhi
,
LI He-Jun
,
FU Qian-Gang
,
ZHANG Yu-Lei
. Investigation of the Multi-coating for High Temperature and Long Life Oxidation Protection of C/C Composites[J]. Journal of Inorganic Materials, 2008
, 23(2)
: 213
-218
.
DOI: 10.3724/SP.J.1077.2008.00213
[1] 孙万昌, 李贺军, 白瑞成, 等(SUN Wan-Chang, et al). 无机
材料学报(Journal of Inorganic Materials), 2005, 20 (3): 671--676.
[2] Fang H T, Yin Z D, Zhu J C. Carbon, 2001, 39 (13): 2035--2041.
[3] 李贺军. 新型炭材料, 2001, 16 (2): 79--80.
[4] 马勤, 阎秉钧, 康沫狂. 稀有金属材料与工程, 1999, 28 (1): 10--13.
[5] 山口正治, 马越佑吉. 金属间化合物. 北京: 科学出版社, 1991. 7.
[6] Vasudevan A K, Petrovic J J. Materials Science and Engineering A, 1992, 155 (1-2): 1--17.
[7] Soojin P, Minkang S. Carbon, 2001, 39 (8): 1229--1235.
[8] 曾燮榕, 李贺军, 杨峥(ZENG Xie-Rong, et al). 硅酸盐学报(Journal of the Chinese Ceramic Society), 1999, 27 (1): 8--14.
[9] Cheng L F, Xu Y D, Zhang L T, et al. Carbon, 1999, 37 (6): 977--981.
[10] Harada Y, Murata Y, Morinaga M. Intermetallics, 1998, 6 (6): 529--535.
[11] Fei G T, Liu L, Zhang L D, et al. Journal of Alloys and Compounds, 1995, 229 (2): 280--282.
[12] 周飞(ZHOU Fei). 硅酸盐学报(Journal of the Chinese Ceramic Society) , 2000, 28 (5): 462--464.
[13] Petrovic J J. Mrs. Bulletin, 1993, 18(7): 35--40.
[14] 艾云龙, 程玉桂, 杨延清, 等. 稀有金属材料与工程, 2005, 34 (6): 962--965.
[15] Zhang B R, Marino F, Sglavo V, et al. Materials Science and Engineering A, 1997, 239-240: 503--506.
[16] Subrahmanyam J, Mohan Rao R. Materials Science and Engineering A, 1994, 183 (1-2): 205--210.
[17] Inui H, Ito K, Nakamoto T, et al. Materials Science and Engineering A, 2001, 314 (1-2): 31--38.
[18] Yanigihara K, Maruyama T, Nagata K. Intermetallics, 1993, 3 (3): 243--251.