The uniform and high intensity reticulated ceramics were fabricated with α-Al2O3 slurry by gel casting injection. The influences of solids volume fractions, dispersant and pH values on the rheological behavior of α-Al2O3 reticulated ceramics were studied. Results show that when pH=9, dispersant=0.5wt%, solid volume fraction=57%, the slurry has a good fluidity, and its viscosity is 140mPa·s. By adopting the argon plasma treating process and the stem grafting of acrylic acid, the absorbed slurry values of the foaming plastics will be changed from 0.42g/cm3 to 0.71g/cm3. The reticulated ceramics fabricated have apparent porosity of 86%, volume density of 0.52g/cm3, and compressive strength of 3.60MPa.
ZHOU Zhu-Fa
,
WANG Shu-Mei
,
WU Ming-Min
. Preparation of Reticulated Ceramics by Gelcasting[J]. Journal of Inorganic Materials, 2008
, 23(1)
: 203
-208
.
DOI: 10.3724/SP.J.1077.2008.00203
[1] 钦征骑, 等．新型陶瓷材料手册. 南京: 江苏科学技术出版社. 1995.
[2] 冯胜山, 陈巨乔．耐火材料, 2002, 36 (4): 235--239 .
[3] 李湘洲．陶瓷, 2005, (5): 47--49.
[4] 陈 哲, 等．十堰职业技术学院学报, 2003, 16 (2): 53--55.
[5] 刘 辉．矿冶工程, 2003, 23 (6): 69--71.
[6] 姬宏杰． 环境污染治理技术与设备, 2003, 4 (12): 73--75.
[7] 张 兰． 山东陶瓷, 2004, 27 (6): 3--6.
[8] 宁红军, 纪士东． 陶瓷, 2005, (6): 19--21.
[9] 朱新文, 江东亮．硅酸盐通报, 2000, (3): 45--51.
[10]王春玲, 纪士东． 陶瓷, 2005, (1): 6--9.
[11] 刘 岩, 黄政仁, 董绍明, 等(LIU Yan, { et al)．无机材料学报(Journal Inorganic Materials), 2005, 20 (2): 305--309.
[12] Brown C C, Green D J． J. Am. Soc., 1994, 77 (6): 1467--1472.
[13] 周竹发, 等．材料工程, 2005, 266 (7): 55--58.
[14] 仝建峰, 陈大明． 航空材料学报, 2003, 23 (3): 50--52.
[15] 曹小刚, 田杰谟．多功能材料, 2001, 32 (5): 523--524; 528.
[16] 唐竹兴．硅酸盐通报, 2001, (2): 23--29.
[17] 江培秋, 李素珍．现代技术陶瓷, 2003, (2): 37--40.
[18] 谢洪德, 王红卫, 等．合成技术及应用, 2003, 18 (4): 17--19.
[19] 杨 超, 邱 高．高分子材料科学与工程, 2001, 17 (6): 30--34.