Nano Mg-Al LDHs were prepared by a hydrothermal method in one step. Effects of precursors, alkalinity of the starting solution, temperature and time on phase purity and crystallite sizes of Mg-Al LDHs were systematically investigated. Reaction products were characterized by powder XRD and SEM. Crystallite sizes of Mg-Al LDHs were determined by the X-ray whole powder pattern fitting method. The optimal parameters for preparing Mg-Al LDHs are keeping the ratio of MgO:Al(OH)3:Na2CO3=2:1:1
at 140℃ for 4h to 10h. The formation mechanism proposed for Mg-Al LDHs is dissociationprecipitiationcrystal growth. The reactant type and hydrothermal conditions may influence the dissociation rate of the precursors, nucleation and growth rates of Mg-Al LDHs, as well as phase combination and crystallite sizes of the reaction products.
WANG Yong-Zai
. Hydrothermal Synthesis Nano Mg-Al LDHs and its Formation Mechanism[J]. Journal of Inorganic Materials, 2008
, 23(1)
: 93
-98
.
DOI: 10.3724/SP.J.1077.2008.00093
[1] Cavani F, Trifiro F, Vaccari A. Catal. Today, 1991, 11: 173-301.
[2] Khan A I, O’Hare D. J. Mater. Chem., 2002, 12: 3191-3198.
[3] Newman S P, Jones W. New J. Chem., 1998. 105-115.
[4] Trifiro F, Vaccari A. Comprehensive Supramolecular Chemistry, Pergamon, Oxford, 1996, 7: 251-291.
[5] Aramendia M A, Borau V, Jimenez C, et al. J. Solid State Chem., 2002, 168: 156-161.
[6] Hickey L, Kloprogge J T, Frost R L. J. Mater. Sci., 1999, 35: 4347-4355.
[7] Labajos F M, Rives V, Ulibarri M A. J. Mater. Sci., 1992, 27: 1546-1552.
[8] Rao M M, Reddy B R, Jayalakshmi M V, et al. Mater. Research Bull., 2005, 40: 347-359.
[9] Zhao Yun, Li Feng, Zhang Rui, et al. Chem. Mater., 2002, 14: 4286-4291.
[10] 冯 桃, 李殿卿, 段 雪．无机化学学报, 2002, 18 (11): 1156-1160.
[11] Xu Zhi-Ping, Lu Guo-Qing. Chem. Mater., 2005, 17: 1055-1062.
[12] Bruker AXS, DIFFRACplus TOPAS P, Version 2.1. 2003, 6. BRUKER AXS GmbH, West Germany.
[13] Labajos F M, Rives V, Ulibarri M A. J. Mater. Sci., 1992, 27: 1546-1552.
[14] Rao M M, Reddy B R, Jayalakshmi M V, et al. Mater. Res. Bull., 2005, 40: 347-359.
[15] Oh J-M, Hwang S-H, Choy J-H. Solid State Ionics, 2002, 151: 285-291.