Self-assembling Magnetic Microspheres by P(St-co-AA) and Fe3O4 Nanoparticles

  • WEN De ,
  • ZENG Hong-Mei ,
  • WANG Yan-Ying ,
  • LAI Qiong-Yu ,
  • JI Xiao-Yang
Expand
  • 1. College of Chemistry, Sichuan University, Chengdu 610064, China; 2. Analytical and Testing Center, Sichuan University, Chengdu 610064, China

Received date: 2007-01-08

  Revised date: 2007-03-13

  Online published: 2008-01-20

Abstract

Uniform P(St-co-AA) microspheres were prepared by microemulsion polymerization. The Fe3O4/P(St-co-AA) microspheres with a high magnetic content were prepared by electrostatic self-assembly using P(St-co-AA) microspheres with Fe3O4 nanoparticles synthesized by co-precipitation. The effects of pH, stirring on the preparation of Fe3O4/P (St-co-AA) were investigated. All samples were characterized by transmission electron microscope (TEM), scanning electron microscope(SEM), X-ray diffraction(XRD), FTIR spectroscope. The magnetic property of the obtained magnetic powder with Fe3O4 single phase was tested by VSM. The results indicate that the average sizes of polymer microspheres P(St-co-AA) with carboxyl and the magnetic powders Fe3O4 are 70nm and 10nm, respectively. Magnetic property measurement shows that the saturated magnetization of the magnetic powders is 69A·m2·kg-1 when the applied field is up to 1.5×106/pi(A/m) at room temperature. The assembled Fe3O4/ P(St-co-AA) with an average size of 800nm is spherical and the content of magnetic powders is 15.8%.

Cite this article

WEN De , ZENG Hong-Mei , WANG Yan-Ying , LAI Qiong-Yu , JI Xiao-Yang . Self-assembling Magnetic Microspheres by P(St-co-AA) and Fe3O4 Nanoparticles[J]. Journal of Inorganic Materials, 2008 , 23(1) : 29 -32 . DOI: 10.3724/SP.J.1077.2008.00029

References

[1] Furusawa K, Anzai C. Colloid & Polymer Sci., 1987, 265 (10): 882--888.
[2] Ding Xiao-Bin, Li Wei, Zheng Zhao-Hui, et al. J. Appl. Polym. Sci., 2001, 79 (10): 1847--1851.
[3] Pich A, Bhattacharya S, Adler H-J P. Polymer, 2005, 46 (4): 1077--1086.
[4] Sun Hanwen, Yu Jiahui, Gong Peijun, et al. Journal of Magnetism and Magnetic Materials, 2005, 294 (3): 273--280.
[5] 刘雪奇, 曾红梅, 赖琼钰, 等. 无机化学学报, 2005, 21 (4): 490--494.
[6] Liu Z L, Yang X B, Yao K L, et al. Journal of Magnetism and Magnetic Materials, 2006, 302 (2): 529--535.
[7] Csetneki M, Kabai Faix, et al. Journal of Polymer Science:Part A:Polymer Chemistry, 2004, 42 (19): 4802--4808.
[8] Ma Zhi-Ya, Guan Yue-Ping, Liu Xian-Xiao, et al. Journal of Applied Polymer Science, 2005, 96 (6): 2174--2180.
[9] 黄忠兵, 唐芳琼. 无机化学学报, 2004, 20 (3): 363--366
[10] Frank Caruso, Andrei S Susha, Michael Giersig, et al.Adv. Mater., 1999, 11 (11): 950--953.
[11] Kim F, Kwan S, Akana J, et al. J. Am. Chem. Soc., 2001, 123 (18): 4360--4361.
[12] Hou Y L, Kondoh H. J. Phys. Chem. B, 2005, 109 (11): 4845--4852.
[13] Jian Jin, Tomokazu Iyoda, Chang Sheng Cao, et al. Angew.Chem. Int. Ed., 2001, 40 (11): 2135--2138.
[14] 答hspace*.12cm鸿, 朱以华(DA Hong, et al). 无机材料学报(Journal of Inorganic Materials), 2002, 17 (4): 867--871.
[15] Boal A K, Ilhan F, Derouchey J E, et al. Nature, 2000, 404 (6779): 746--748.
[16] 马光辉, 苏志国. 高分子微球材料, 第一版. 北京: 化学工业出版社, 2005. 190--200.
[17] 张立德, 牟季美. 纳米材料和纳米结构, 第一版. 北京: 科学出版社, 2001. 147--148.
[18] 吴谋成. 仪器分析, 第一版. 北京: 科学出版社, 2003. 70--90.
[19] 杨喜云, 龚竹青. 中南大学学报(自然科学版), 2005, 36 (2): 243--247.
Outlines

/