Synthesis of (Y,Gd)2O3:Eu (YGO:Eu) Nano-Powder and Fabrication of Transparent Ceramics

  • LI Xiao-Dong ,
  • XIU Zhi-Meng ,
  • BAI Li-Li ,
  • GAO Tie ,
  • LIU Yi-Nong ,
  • HU Xiao-Zhi ,
  • SUN Xu-Dong
Expand
  • (1. The Key Laboratory for Anisotropy and Texture of Materials (Ministry of Education), Northeastern University, Shenyang 110004, China; 2. The Key Laboratory of Electromagnetic Processing of Materials (Ministry of Education), Northeastern University, Shenyang 110004, China; 3. School of Mechanical Engineering, the University of Western Australia, Crawley WA 6009, Australia)

Received date: 2006-11-17

  Revised date: 2006-12-21

  Online published: 2007-11-20

Abstract

The synthesis of nano-sized Y1.34Gd0.6Eu0.06O3 (YGO:Eu) powder by using an AHC (ammonium hydrogen carbonate) precipitation technique was investigated. The precursor powders obtained were of crystalline and indexed to yttrium gadolinium normal carbonate. On calcination, the precursor powders were converted to crystalline yttrium gadolinium oxide at 600℃. The powder calcined at 1100℃ show better sintering behavior, mainly due to their narrowest particle size distribution and finest average particle size. Transparent YGO ceramics were prepared by sintering at 1670℃ for 2h in vacuum using the powders calcined at 1100℃. The YGO ceramics shows a high in-line transmittance of 74.6% in the visible-light region, much higher than that of transparent Y2O3 ceramics prepared by the same process.


Cite this article

LI Xiao-Dong , XIU Zhi-Meng , BAI Li-Li , GAO Tie , LIU Yi-Nong , HU Xiao-Zhi , SUN Xu-Dong . Synthesis of (Y,Gd)2O3:Eu (YGO:Eu) Nano-Powder and Fabrication of Transparent Ceramics[J]. Journal of Inorganic Materials, 2007 , 22(6) : 1089 -1094 . DOI: 10.3724/SP.J.1077.2007.01089

References

[1] Greskovich C D, Duclos S. Ann. Rev. Mater. Sci., 1997, 27: 69--77.
[2] Nakamura R. J. Am. Ceram. Soc., 1999, 82 (9): 2407--2410.
[3] Lempicki A, Brecher C, Szupryczynski P, et al. Nucl. Instrum. Methods, 2002, A488 (3): 579--590.
[4] Duclos S, Greskovich C D, Lyons R J, et al. Nucl. Instrum. Methods, 2003, A505 (1-2): 68--71.
[5] Kim Young Kwan, Kim Ho Kyung, Kim Do Kyung, et al. J. Mater. Res., 2004, 19 (2): 413--416.
[6] Kim Young Kwan, Kim Ho Kyung, Kim Do Kyung, et al. Nucl. Instrum. Methods, 2004, B225 (3): 392--396.
[7] Chen J Y, Shi Y, Shi J L. J. Mater. Res., 2004, 19 (12): 3586--3591.
[8] Li H L, Liu X J, Huang L P. J. Am. Ceram. Soc., 2005, 88 (11): 3226--3228.
[9] 陈积阳, 施 鹰(CHEN Ji-Yang, et al). 无机材料学报(Journal of Inorganic Materials), 2006, 21 (1): 157--161.
[10] Saito N, Matsuda S, Ikegami T. J. Am. Ceram. Soc., 1998, 81 (8): 2023--2028.
[11] 吴文远. 稀土冶金学. 北京: 化学工业出版社, 2005. 171--173.
[12] Li J G, Ikegami T, Lee J H, et al. J. Mater. Res., 2000, 15 (11): 2375--2386
[13] Head E L, Holly C E Jr. Rear Earth Research II., London: Gordon and Breach, 1964. 51--57.
[14] Head E L, Holly C E Jr. Rare Earth Research III, London: Gordon and Breach, 1965. 707--712.
[15] Li J G, Ikegami T, Mori T, et al. J. Am. Ceram. Soc., 2004, 87 (6): 1008--1013.
Outlines

/