Effect of Al as Active Filler on Properties of Preceramic-derived Multi-phased Ceramics

  • ZHU Yun-Zhou ,
  • HUANG Zheng-Ren ,
  • DONG Shao-Ming ,
  • YUAN Ming ,
  • JIANG Dong-Liang
Expand
  • (1. Shanghai Institute of Ceramics, Chinese Academy of Sciences, Shanghai 200050, China; 2. Graduate University of the Chinese Academy of Sciences, Beijing 100049, China)

Received date: 2006-10-09

  Revised date: 2006-12-18

  Online published: 2007-09-20

Fold

Abstract

Al and SiC powders were chosen as active filler and inert filler, respectively, for the fabrication of preceramic-derived multi-phased ceramics, using polycarbosilane as preceramic precursor. The effects of pyrolysis temperature and soaking time on ceramic yield, linear shrinkage, mechanical properties and microstucture were investigated. Volume expansion was observed
due to the reaction of Al particles with carbon-containing pyrolysis products and reactive atmosphere. The derived ceramics with small shrinkage and high ceramic yield could meet the demand of near net shaping process. After the ceramic composite was pyrolyzed at 1000℃ for 1h, the bending strength reached 293MPa with the shrinkage of 0.08% and ceramic yield of 99.68%.

Key words： preceramic precursor; active filler; linear shrinkage; ceramic yield

Cite this article

ZHU Yun-Zhou , HUANG Zheng-Ren , DONG Shao-Ming , YUAN Ming , JIANG Dong-Liang . Effect of Al as Active Filler on Properties of Preceramic-derived Multi-phased Ceramics
[J]. Journal of Inorganic Materials, 2007 , 22(5) : 959 -962 . DOI: 10.3724/SP.J.1077.2007.00959

References

[1] Erny T, Seibold M, Jarchow O, et al. J. Am. Ceram. Soc., 1993, 76 (1): 207--213.
[2] Greil P. J. Euro. Ceram. Soc., 1998, 18: 1905--1914.
[3] Deniz Akkas H, Lutfi Ovecoglu M, Tanoglu M. J. Euro. Ceram. Soc., 2005, 26 (15): 3441--3449.
[4] 陈朝辉. 前驱体结构陶瓷. 国防科技大学出版社, 2003. 1--34.
[5] Greil P. J. Am. Ceram. Soc., 1995, 78 (4): 835--848.
[6] 谢征芳, 陈朝辉, 肖加余(Xie Zheng-Fang, et al). 硅酸盐学报(Journal of the Chinese Ceramic Society), 2002, 30 (3): 382--386.
[7] 周 游. 反应热解聚合物前驱体制备复相陶瓷的研究. 中国科学院上海硅酸盐研究所博士学位论文, 1995.
Options
Outlines

/

〈 〉