Dry spinning performance of PCSsolution and self crosslinking process of the PCS fiber as-spun were studied by viscosity, gel content and XRD techniques. The composition, structure and mechanical properties of SiC fibers were also characterized. Results show that the optimum spinning viscosity of PCS/xylene solution is 18.0-22.0Pa·s, self crosslinking process of the PCS fiber by dry-spun begins at 250℃ during pyrolysis process, and finishes at 550℃ to form a network structure which does not melt or dissolue. The oxygen content of the final SiC fibers is decreased to about 3.6wt%. SiC fibers prepared by dry spinning have a better β-SiC microcrystalline structure and show better oxidation resistance than those prepared by the oxidation curing.
XUE Jin-Gen
,
WANG Ying-De
,
SONG Yong-Cai
. Preparation of Low Oxygen SiC Fiber by Dry Spinning[J]. Journal of Inorganic Materials, 2007
, 22(4)
: 681
-684
.
DOI: 10.3724/SP.J.1077.2007.00681
[1] Laine R M, Babonneau F. Chemical Materials, 1993, 5: 260--279.
[2] Ichikawa H, Machino F, Mitsuno S. Journal of Materials Science, 1986, 21: 4352--4358.
[3] Shimoo T, Morita T, Okamura K. Journal of the American Ceramic Societ., 2001, 84 (12): 2975--2980.
[4] Takeda M, Urano A, Sakamoto J, et al. Journal of Nuclear Materials, 1998, 258-263: 1594--1599.
[5] 楚增勇, 冯春祥, 宋永才, 等(CHU Zeng-Yong, et al). 无机材料学报(Journal of Inorganic Materials), 2002, 17 (2): 193--201.
[6] William Toreki. Composites Science and Technology, 1994, 51: 145--159.
[7] 薛金根, 王应德, 宋永才, 等(Xue Jin-Gen, et al). 现代化工(Modern Chemical Industry), 2006, 26 (6): 48--50.
[8] Ly H Q, Taylor R, Day R J, et al. Journal of Materials Science, 2001, 36: 4045--4057.