Adv. Search
Journal of Inorganic Materials

Journal of Inorganic Materials >

2007 , Vol. 22 >Issue 4: 637 - 641

DOI: https://doi.org/10.3724/SP.J.1077.2007.00637

Research Paper

Synthesis and Characterization of LiNi1/3Co1/3Mn1/3O2 as a Cathode Material for Lithium Batteries by Ultrasonic Spray Pyrolysis

  • LIU Zhi-Min ,
  • HU Guo-Rong ,
  • FANG Zheng-Sheng ,
  • ZHANG Xin-Long ,
  • LIU Ye-Xiang
Expand
  • School of Metallurgical Science and Engineering, Central South University, Changsha 410083, China

Received date: 2006-07-14

  Revised date: 2006-10-11

  Online published: 2007-07-20

Fold

Abstract

Spherical morphology LiNi1/3Co1/3Mn1/3O2 as a cathode aterial of lithium ion batteries was successfully synthesized by an ultrasonic spray pyrolysis method. The effects of different precursor solution on the morphology of particles were investigated. The reasons of morphology difference were analysed by using the process mechanism of spray pyrolysis. In addition, the impacts of various post reatment sintering time on electrochemical performances of the samples were characterized. Experimental results show that the cathode material synthesized by ultrasonic spray pyrolysis using nitrate as precursor solution, followed by sintering at 900℃ for 6h, exhibits excellent electrochemical properties. In the voltage range of 3.0--4.3V, initial discharge capacity of the sample is 157.7mAh · g-1 and its capacity retains 146.6mAh·g-1 after 40 cycles.

Key words： lithium-ion battery; ultrasonic spray pyrolysis; LiNi1/3Co1/3Mn1/3O2

Cite this article

LIU Zhi-Min , HU Guo-Rong , FANG Zheng-Sheng , ZHANG Xin-Long , LIU Ye-Xiang . Synthesis and Characterization of LiNi1/3Co1/3Mn1/3O2 as a Cathode Material for Lithium Batteries by Ultrasonic Spray Pyrolysis[J]. Journal of Inorganic Materials, 2007 , 22(4) : 637 -641 . DOI: 10.3724/SP.J.1077.2007.00637

References

[1] Ohzuku T, Makimura Y. Chem. Lett., 2001, 7: 642--643.
[2] Shaju K M, Subba Rao G V, Chowdari B V R. Electrochim. Acta, 2002, 48: 145--151.
[3] Luo X F, Wang X Y, Liao L. J. Power Source, 2006, 158: 654--658.
[4] Cho T H, Park S M, Yoshio M. J. Power Source, 2005, 142: 306--312.
[5] Chen Y, Wang G X, Konstantinov K, et al. J. Power Source, 2003, 119-121: 184--188.
[6] Lee M H, Kang Y J, Myung S T, et al. Electrochimica Acta, 2004, 50: 939--948. [7] 胡国荣, 刘智敏, 方正升, 等. 功能材料, 2005, 36 (03): 335--339.
[8] 徐志军, 初瑞清, 李国荣, 等(XU Zhi-Jun, et al). 无机材
料学报(Joural of Inorganic Material), 2004, 19 (6): 1240--1248.
[9] Che S L, Sakurai O, Shinozaki K, et al. J. Aerosol Sci, 1998, 29: 271--278.
[10] Messing G L, Zhang S C, Jayanthi G V. J. Am. Ceram. Soc., 1993, 76 (11): 2707--2719.
[11] Matijevic E, Hsu W P. J. Colloid Interface Sci., 1987, 118: 506--523.
[12] Sordelet D, Akinic M. J. Colloid Interface Sci., 1988, 122: 47--59.
[13] Roh H S, Kang Y C, Park S B. J. Colloid Interface Sci., 2000, 228: 195--199.
Options
Outlines

/

〈 〉