Adv. Search
Journal of Inorganic Materials

Journal of Inorganic Materials >

2007 , Vol. 22 >Issue 5: 894 - 900

DOI: https://doi.org/10.3724/SP.J.1077.2007.00894

Research Paper

Preparation and Electrochemical Performance of Copper Oxide/Porous Carbon Composites as Electrode Materials for Electrochemical Capacitors

  • LI Qiang ,
  • LI Kai-Xi ,
  • GU Jian-Yu ,
  • FAN Hui ,
  • LU Chun-Xiang
Expand
  • 1. Key Laboratory of Carbon Materials, Institute of Coal Chemistry, Chinese Academy of Sciences, Taiyuan 030001, China; 2. Graduate University of the Chinese Academy of Sciences, Beijing 100049, China

Received date: 2006-10-18

  Revised date: 2006-12-04

  Online published: 2007-09-20

Fold

Abstract

Copper oxide/porous carbon composite materials were prepared by a chemical deposition method. The effects of heat treatment temperature and copper oxide loading amount on the physical and chemical properties of the composites were investigated. The results show that heat treatment can change species of copper oxide, and these species can influence the electrochemical performance of the composite electrode materials. After loading 20wt％ copper oxide, a relatively strong peak current appears in the cyclic voltammograms of copper oxide/porous carbon composite electrode, but its electrochemical capability is unstable. The decrease of the loading amount of copper oxide is responsible for the improvement of electrochemical stability. When 3wt％ of copper oxide materials is loaded, the single-electrode specific capacitance of the composite electrode reaches 325F/g, which is higher than that of pure porous carbons (256F/g).

Key words： electrochemical capacitors; copper oxide/porous carbon; composite electrode materials; chemical deposition

Cite this article

LI Qiang , LI Kai-Xi , GU Jian-Yu , FAN Hui , LU Chun-Xiang . Preparation and Electrochemical Performance of Copper Oxide/Porous Carbon Composites as Electrode Materials for Electrochemical Capacitors[J]. Journal of Inorganic Materials, 2007 , 22(5) : 894 -900 . DOI: 10.3724/SP.J.1077.2007.00894

References

[1] Zhang Yan-ge, Wang Shu-tao, Qian Yi-tai, et al. Solid State Sciences, 2006, 8: 462--466.
[2] Grugeon S, Laruelle S, Herrera-Urbina R, et al. J. Electrochem. Soc., 2001, 148 (4): A285--A292.
[3] Zhang J, Xie S, Wei X, et al. J Power Sources, 2004, 137: 88--92.
[4] Debart A, Dupont L, Poizot P, et al. J. Electrochem. Soc., 2001, 148 (11): A1266--A1274.
[5] Hwang Shu-Rong, Teng Hsisheng. J. Electrochem. Soc., 2002, 149 (5): A591--A596.
[6] 孟庆函. 双电层电容器电极材料的制备及电化学性能研究. 中国科学院山西煤炭化学研究所. 博士学位论文, 2002.
[7] He Jian-Bo, Lu Dao-Yong, Jin Guan-Ping. Appl. Surf. Sci., 2006, 253: 689--697.
[8] 崔宝臣, 马丽景, 白守礼, 等. 化工进展, 2004, 23 (5): 541--544.
[9] 蔡欣, 夏晓红, 范中丽, 等. 华中师范大学学报(自然科学版), 2004, 38 (1): 44--46.
[10] WU Zhengcui, SHAO Mingwang, ZHANG Wu, et al. J. Crystal Growth, 2004, 260: 490--493.
[11] Wang Zhenghua, Chen Xiangying, Liu Jianwei, et al. Solid State Commun., 2004, 130: 585--589.
[12] Berlouis L E A, Mamman D A, Azpuru I G. Surface Science, 1998, 408: 173--181.
Options
Outlines

/

〈 〉