CdSe nanorods with different structure phases were prepared by a hydrothermal method, and the products were characterized with TEM, SEM, XRD, TGA-DTA. The results show that the CdSe nanorod with zinc blende structure is formed at 200℃ reaction temperature. At 240℃ reaction temperature, the wurtzite structure CdSe nanorod can be obtained.The IPCE of the wurtzite structure CdSe nanorod film electrode is higher than that of zinc blende structure CdSe nanorod film electrode. The wavelength with the max IPCE value for the CdSe/PMeT composite film electrode appears as red shift.
HAO Yan-Zhong
,
YIN Zhi-Gang
. Preparation and Photoelectrochemical Study of CdSe Nanorods with Different Structure Phases[J]. Journal of Inorganic Materials, 2007
, 22(3)
: 413
-417
.
DOI: 10.3724/SP.J.1077.2007.00413
[1] 聂秋林, 袁求理, 徐铸德(NIE Qiu-Lin, et al). 无机材料学报(Journal of Inorganic Materials), 2004, 19 (6): 1411--1414.
[2] 赵启涛, 候利松, 黄瑞安, 等(ZHAO Qi-Tao, et al). 无机材料学报(Journal of Inorganic Materials), 2004, 19 (3): 477--480.
[3] 曹广胜, 俞庆森, 董喜贵,等(CAO Guang-Sheng, et al). 无机材料学报(Journal of Inorganic Materials), 2005, 20 (4): 815--820.
[4] 张俊松, 马娟, 陈秀梅,等. 南京师大学报, 2004, 27 (2): 61--62.
[5] Li Y D, Liao H W, Ding Y, et al. J. Chem. Mater., 1998, 10 (9): 2301--2303.
[6] Wang W Z, Geng Y, Yan P, et al. Inorgnic Chemistry Communications 2, 1999. 83--85.
[7] Yu S H, Wu Y S, Yang J, et al. J. Chem. Mater., 1998, 10: 2309--2312.
[8] Xu D S, Shi X S. J. Phys. Chem., 2000, 104 (21): 5061--5063.
[9] Trindade T,O’ Brien P, et al. J. Mater. Chem., 1996, 6 (3): 343-346; Adv. Mater., 1996, 8 (2): 161--163.
[10] Huynh W U, Peng X G, Alivisatos A P. Adv. Mater., 1999, (11): 923-927.
[11] Huynh W U, Pittmer J J, Trclemariam D J, et al. Phys. Rev., 2003, 67 (11): 115326--115331.
[12] Manna L, Milliron D J, Meisel A. Nat. Mater., 2003, 2: 382--386.
[13] Peng Q, Dong Y J, Deng Z X, et al. Inorg. Chem., 2002, 41 (20): 5249--5254.
[14] 李东升, 吕功煊. 高等学校化学学报, 2002, 23 (4): 685--689.
[15] Liu J S, Tanaka T, Sivula K, et al. J. Am. Chem. Soc., 2004, 126: 6550--6551.
[16] 郝彦忠, 蔡春立. 物理化学学报, 2005, 21 (12): 1395--1398.
[17] Snaith H J, Whiting G L, Sun B, et al. Nano Letters, 2005, 5 (9): 1653--1657.
[18] 郝彦忠, 武文俊. 化学学报, 2005, 63 (3): 215--218.
[19] 武文俊, 郝彦忠. 感光科学与光化学, 2004, 22 (5): 378--382.