Zn(NO3)2为原料,CTAB为形貌控制剂, 采用水热合成技术制备了一维氧化锌粉体. 采用X射线衍射(XRD)、透射电镜(TEM)、扫描电镜(SEM)等测试技术对产物的相组成和微观形态进行了表征和分析, 结果表明一维氧化锌属于六方晶系, 分散性好, 纯度高, 直径～200nm, 长度～5μm. 用该粉体制成烧结型旁热式气敏元件, 测试其气敏性能. 结果表明, 在170℃左右对10ppm的三甲胺、甲醇等还原性气体有很好的响应. 文中对一维材料的气敏机理也进行了讨论.
Zn(NO3)2 was used as the raw material to prepare one-dimension ZnO through a hydrothermal technique with CTAB controlling ZnO morphology. The products were characterized by X-ray diffraction(XRD), transmission electron microscope(TEM) and scanning electron microscope(SEM). Gas sensors were made by using the ZnO nanorads and their gas sensitivities were measured. The result shows that the ZnO nanorods have lower working temperature than granulated ZnO and have very good sensitivity to 10ppm trimethylamine (TMA), methanol, ammonia, acetone and ethanol at the working temperature of 170℃. The gas sensitivity mechanism of the ZnO rods was discussed.
1 郑占丰, 高学平, 潘桂玲等. 无机化学学报, 2004. 4 (20): 488-492.
2 Park Won Il, Yi Gyu-Chul. J. Advanced Materials, 2004, 16: 87-90.
3 艾仕云, 金利通, 周杰. 无机化学学报, 2005, 2 (21): 270-272.
4 Zhang Yongsheng, Yu Ke, Jiang Desheng, et al. J . Applied Surface Science, 2005, 242: 212-217.
5 Kong J, Franklin N R, Zhou C, et al. J. science, 2000, 287: 622-625.
6 Heo Y W, Tien L C, Norton D P. J. Applied Physics Letters, 2004, 9 (85): 2002-2004.
7 徐甲强, 潘庆谊, 孙雨安, 等. 无机化学学报, 1998, 14: 354-359.
8 Sun X M, Chen X, Deng Z X, et al. J. Materials Chemistry and Physics, 2002, 78: 99-104.
9 宋旭春, 徐铸德, 陈卫祥, 等. 无机化学学报, 2004, 2: 186-190.
10 Zhang Hui, Yang Deren, Ji Yujie, et al. J. Phys. Chem. B, 2004, 108: 3955-3958.
11 祝柏林, 谢长生. 传感技术学报, 2002. 12(4): 353-359.