高级检索
无机材料学报

无机材料学报 >

2010 , Vol. 25 >Issue 6: 621 - 625

DOI: https://doi.org/10.3724/SP.J.1077.2010.00621

研究论文

微结构对Bi2Sr2Co2Oy化合物电性能的影响

  • 高文斌 ,
  • 张 莉 ,
  • 唐新峰
展开
  • (武汉理工大学 材料复合新技术国家重点实验室, 武汉 430070)

收稿日期: 2009-06-24

  修回日期: 2009-10-27

  网络出版日期: 2010-05-12

基金资助

国家973计划项目(2007CB607501)

收起

Influence of Microstructure on the Electrical Properties of Bi2Sr2Co2Oy Compound

  • GAO Wen-Bin ,
  • ZHANG Li ,
  • TANG Xin-Feng
Expand
  • (State Key Laboratory of Advanced Technology for Materials Synthesis and Processing, Wuhan University of Technology,   Wuhan 430070, China)

Received date: 2009-06-24

  Revised date: 2009-10-27

  Online published: 2010-05-12

Fold

摘要

通过溶胶-凝胶法制备单相Bi2Sr2Co2Oy化合物, 通过添加PEG20000和超声分散对化合物粉体微结构进行调控, 采用SPS烧结得到了致密的块体. 探索了微结构对Bi2Sr2Co2Oy化合物电性能的影响规律. 结果表明,添加PEG20000和超声分散可以明显降低Bi2Sr2Co2Oy化合物粉体的晶粒尺寸, 使烧结块体的晶粒尺寸大幅度减小, 从而显著提高材料的电性能. 温度为873K时, 添加PEG20000并超声处理所制备样品烧结块体获得了最高ZT值0.041.

关键词： Bi2Sr2Co2Oy; PEG; 超声; 电性能

本文引用格式

高文斌 , 张 莉 , 唐新峰 . 微结构对Bi2Sr2Co2Oy化合物电性能的影响[J]. 无机材料学报, 2010 , 25(6) : 621 -625 . DOI: 10.3724/SP.J.1077.2010.00621

Abstract

Single phase Bi2Sr2Co2Oy compound was synthesized by Sol-Gel method, using PEG20000 and ultrasonic treatment to optimize microstructure of powders, and bulk materials were gained after SPS technique. The influence of microstructure on electrical properties of Bi2Sr2Co2Oy compound was investigated. The results show that adding of PEG20000 and ultrasonic treatment can decrease the size of powders obviously, the grain size of bulk materials decreases greatly, so the electrical properties of material increased. Bulk materials synthesized from the powders prepared with adding PEG20000 and ultrasonic treatment gain the highest ZT value of 0.041 at 873K.

Key words： Bi2Sr2Co2Oy; PEG; ultrasonic; electrical properties

参考文献

[1]Terasaki I, Sasago Y, Uchinokura K. Larger thermoelectric power in NaCo2O4 single crystals. Phys. Rev. B: Condens Matter, 1997, 56(20): R12685-R12687.

[2]Lee Minhyea, Viciu Liliana, Li Lu, et al. Large enhancement of the thermopower in NaxCoO2 at high Na doping. Nature Materials, 2006, 5(7): 537-540.

[3]Ito Mikio, Furumoto Daisuke. Microstructure and thermoelectric properties of NaxCo2O4/Ag composite synthesized by the polymerized complex method. Journal of Alloys and Compounds, 2008, 450 (1/2): 517-520.

[4]Wang Dongli, Chen Lidong, Yao Qin. High-temperature thermoelectric properties of Ca3Co4O9+x with Eu substitution. Solid State Communications, 2004, 129 (9): 615-618.

[5]Wang Y, Rogado N S, Cava J R, et al. Spin entropy as the likely source of enhanced thermoelectric in NaxCo2O4. Nature, 2003, 423: 425-428.

[6]邢学玲, 闵新民．钴酸盐类氧化物热电材料的研究进展．材料导报, 2006, 20(2): 47-53

[7]Funahashi Ryoji, Shikano Masahiro. Bi2Sr2Co2Oy whiskers with high thermoelectric figure of merit. Appl. Phys. Lett., 2002, 81(8): 1459-1461.

[8]Funahashi Ryoji, Matsubara Ichiro, Sodeoka Satoshi. Thermoelectric properties of Bi2Sr2Co2Ox polycrystalline materials. Appl. Phys. Lett., 2000, 76(17): 2385-2387.

[9]包 南, 孙 剑, 谢 晴, 等. PEG辅助纳米TiO2的可控制备及其光催化活性.传感技术学报,2006, 19(5):2354-2358

[10]应皆荣, 万春荣, 姜长印, 等. 聚乙二醇对无机盐的胶束增溶作用及在溶胶配制中的应用. 功能材料, 2001, 32(2): 118-120.

[11]王俊中, 胡 源, 陈祖耀(WANG Jun-Zhong, et al). 超声化学制备纳米材料的研究进展. 稀有金属材料与工程(Rare Metal Mat. Eng.), 2003, 32(8): 585-590.
Options
文章导航

/

〈 〉