Preparation of Porous Scaffolds of Borosilicate Bioglass

  • LIU Xin ,
  • YAO Ai-Hua ,
  • WANG De-Ping ,
  • HUANG Wen-Hai ,
  • FU Hai-Luo ,
  • ZHAO Di ,
  • LU Wei-Jia ,
  • PAN Hao-Bo
Expand
  • 1. Institute of Bioengineering and Information Technology Materials, School of Material Science and Engineering, Tongji University, Shanghai 200092, China; 2. Faculty of Medicine, University of Hong Kong, Hong Kong 999077, China

Received date: 2007-04-24

  Revised date: 2007-06-22

  Online published: 2008-03-20

Fold

摘要

Na2O-CaO-SiO2-P2O5-B2O3系硼硅酸盐生物玻璃是一类具有良好生物活性和降解性能的组织工程材料. 本研究中, 采用有机泡沫浸渍法, 乙醇作溶剂, 乙基纤维素作添加剂, 将硼硅酸盐玻璃粉体制备成具有三维连通网状结构的组织工程多孔支架. 通过调节浆料的固相含量和乙基纤维素含量, 改善坯体的涂覆量, 在支架孔径为300~500μm,孔隙率高于80%时, 使支架抗压强度从0.03MPa提高到0.36MPa. 根据蜂窝状结构模型分析, 发现采用高强度玻璃, 优化浆料是改善多孔材料结构和力学性能的有效途径. 用该模型理论指导, 由Na2O-K2O-MgO-CaO-SiO2-P2O5-B2O3系统制成的另一种硼硅酸盐玻璃支架, 其抗压强度可达5~8MPa. 实验表明有机泡沫浸渍法在制备组织工程支架中有广泛的应用前景.

关键词： 有机泡沫浸渍法; 硼硅酸盐生物活性玻璃; 多孔支架; 浆料

本文引用格式

刘欣 , 姚爱华 , 王德平 , 黄文hai , 付海罗 , 赵荻 , 吕维加 , 潘浩波 . 硼硅酸盐生物活性玻璃多孔支架的制备[J]. 无机材料学报, 2008 , 23(2) : 322 -326 . DOI: 10.3724/SP.J.1077.2008.00322

Abstract

A borosilicate bioglass in Na2O-CaO-SiO2-P2O5-B2O3 system is a bioactive and biodegradable material for tissue engineering. In this study, the bioactive porous scaffolds with three-dimensional interconnection were fabricated by replication technique, using borosilicate bioglass powder to form slurry with ethanol as solvent and ethyl-cellulose as additive. The compressive strength of scaffolds increases from 0.03MPa to 0.36MPa by adjusting the slurry load, the solid concentration and the ethyl-cellulose concentration in the slurry, while the pore size of scaffolds remains in the rangeot 300--500μm and the porosity maintains over 80%. According the analysis on Cellular Structure Model, it is suggested that employing high strength glass and optimizing slurry composition are effective approaches to improve cellular structure and increase scaffold strength. The compressive strength of another borosilicate glass scaffolds made from Na2O-K2O-MgO-CaO-SiO2-P2O5-B2O3 system can reach 5--8MPa based on the theory. These experiments show that the replication technique is a promising way to prepare bioglass scaffolds.

Key words： replication technique; borosilicate bioglass; scaffolds; slurry

参考文献

[1] Hutmacher D W. Biomaterials, 2000, 21 (24): 2529--2543.
[2] Jones J R, Ehrenfried L M, Hench L L. Biomaterials, 2006, 27 (7): 964--973.
[3] 鞠银燕, 陈晓峰, 王迎军. 中国陶瓷, 2005, 41 (3): 23--26.
[4] 田杰谟, 李信勇, 张勇, 等. 功能材料, 2002, 33 (6): 656--657.
[5] 朱新文, 江东亮, 谭寿洪(ZHU Xin-Wen, et al). 无机材料学报(Journal of Inorganic Materials), 2001, 16 (6): 1144--1149.
[6] Gibson L J. Journal of Biomechanics, 2005, 38 (9): 377--399.
[7] Marion N W, Liang W, Reilly G, et al. Mechanics of Advanced Material and Structures, 2005, 12 (3): 239--246.
[8] Huang W H, Day D E, Kittiratanapiboon K, et al. Journal of Materials Science: Materials in Medicine, 2006, 17: 583--596.
[9] Huang W H, Rahaman M N, Day D E, et al. Glass Technology: European Journal of Glass Science and Technology Part A, 2006, 47 (6): 647--658.
[10] Yao A H, Wang D P, Fu Q, et al. Chinese Science Bulletin, 2007, 52 (2): 272--276.
[11] 宁佳, 王德平, 黄文#[49], 等. 硅酸盐学报, 2006, 34 (11): 1326--1330.
[12] 果世驹. 粉末烧结理论, 第一版. 北京: 冶金工业出版社, 1998. 166--170.
[13] Hyppola R, Husson I, Sundholm F. International Journal of Pharmaceutics, 1996, 133 (1-2): 161--170.
[14] Graham C, Michael E A, John E H. Pharmaceutical Coating Technology. London: Bristol PA: Taylor & Francis, 2002. 9--10.
[15] Zhu X W, Jiang D L, Tan S H. Materials Letters, 2001, 51 (4): 363--367. [16] Oliveira F A C, Dias S, Vaz M F, et al. Journal of the European Ceramic Society, 2006, 26 (1-2): 179--186.
[17] Chen Q Z, Thompson I D, Boccaccini A R. Biomaterials, 2006, 27 (11): 2414--242.
[18] Fu Q, Rahaman M N, Bal B S, et al. Journal of Biomedical Materials Research Part A, 2007, 82A (1): 222--229.

Options
文章导航

/

〈 〉