用共沉淀法制备的平均粒径为50nm的钇铝石榴石纳米粉体为原料, 以0.5wt%的正硅酸已脂为烧结助剂, 采用两步烧结的工艺路线制备了YAG透明陶瓷. 将成型后的素坯在真空炉内首先加热到一个较高的温度(1700～1800℃), 再快速降温至较低温度(1500～1600℃), 并在此较低温度下保温10h. 通过抑制晶界迁移, 促进晶界扩散, 在较低的保温温度下制备了YAG透明陶瓷. 当两步烧结温度分别为1800℃和1550℃时, YAG透明陶瓷在可见光下的透过率为72%, 晶粒尺寸为6μm.
Well dispersed yttrium aluminum garnet (YAG) nanopowders with mean particle size of about 50nm synthesized by modified co-precipitation method were used to sinter YAG transparent ceramics with 0.5wt% TEOS as sintering additive by two step sintering process. The samples were first heated to a higher temperature ranging from 1700℃ to 1800℃, then cooled down to a lower temperature ranging from 1500℃ to 1600℃, and held at the lower temperature for 10h. Grain-boundary migration is suppressed and grain-boundary diffusion is promoted during the two step sintering process. When the two step sintering temperatures are 1800℃ and 1550℃, the microstructure of YAG is homogeneous with average grain size of 6μm without abnormal grain growth and the transmittance of the specimen is 72.0%
[1] Ikesue A, Furusato I, Kamata K. J. Am. Ceram. Soc., 1995, 78 (1): 225--228.
[2] Ikesue A, Kinoshita T, Kamata K, et al. J. Am. Ceram. Soc., 1995, 78 (4): 1033--1040.
[3] Wu Yusong, Li Jiang, Qiu Fagui, et al. Ceramics International, 2006, 32 (6): 785--788.
[4] Zhang Huashan, Han Hui, Su Chunhui, et al. Materials Science and Engineering A, 2007, 445--446 (1--2): 180--185.
[5] Li Xia, Li Qiang, Wang Jiyang, et al. Optical Materials, 2007, 29 (5): 528--531.
[6] Liu Min, Wang Shiwei, Zhang Jian. Journal of Rare Earths, 2006, 24 (6): 732--735.
[7] Lee Sang-Ho, Kochawattana Sujarinee L. Messing Gary, et al. J. Am. Ceram. Soc., 2006, 89 (6): 1945--1950.
[8] Ikesue A, Aung Yan Lin, Yoda T, et al. Optical Materials, (2006), doi:10.1016/j.optmat.2005.12.013.
[9] Wen Lei, Sun Xudong. J. Eur. Ceram. Soc., 2004, 24 (9): 2681--2688.
[10] Chaima R, Marder-Jaeckel R, Shen J Z. Materials Science and Engineering A, 2006, 429 (1--2): 74--78.
[11] Chen Zhi-Hui, Yang Yun, Li Jiang-Tao, et al. J. Alloy & Comp.,
doi:10.1016/j.jallcom.2006.06.084.
[12] Chen I -Wei, Wang X H. Nature, 2000, 404 (9): 167--171.
[13] Kim Hai-Doo, Park Young-Jo, Han Byung-Dong, et al. Scripta Materialia, 2006, 54 (4): 615--619.
[14] Li Jiangong, Ye Yinping. J. Am. Ceram. Soc., 2006, 89 (1): 139--143.
[15] Chen P L, Chen I W. J. Am. Ceram. Soc., 1997, 80 (3): 637--645