研究论文

溶胶凝胶-自燃烧法合成La 9.33Si 6O26超细粉体

  • 田长安 ,
  • 刘俊亮 ,
  • 蔡 俊 ,
  • 曾燕伟
展开
  • (南京工业大学 材料科学与工程学院, 南京 210009)

收稿日期: 2006-12-27

  修回日期: 2007-02-04

  网络出版日期: 2008-01-20

Synthesis of La9.33Si6O26 Single-phase Ultrafine Powder by Sol-Gel Self-combustion Method

  • TIAN Chang-An ,
  • LIU Jun-Liang ,
  • CAI Jun ,
  • ZENG Yan-Wei
Expand
  • (Nanjing University of Technology, School of Materials Science & Engineering, Nanjing 210009, China)

Received date: 2006-12-27

  Revised date: 2007-02-04

  Online published: 2008-01-20

摘要

用柠檬酸和乙二醇做络合剂和燃料, 硝酸盐做氧化剂, 用氨水调节溶胶pH值, 通过溶胶凝胶-自燃烧法一步合成了可用于固体氧化物燃料电池(SOFC)的新型固体电解质La9.33Si6O26. 用XRD、TEM等分析方法对合成粉体进行了物相测定与形貌观察, 并初步考察了粉体的烧结性能. 结果表明:通过工艺参数的有效设计, 溶胶-凝胶和自燃烧过程可以在短时间内达到合成所需要的高温, 一步合成粒径约为150~300nm的单相La9.33Si6O26超细粉体, 其烧结温度比固相法制备的粉体的烧结温度约低200℃.

本文引用格式

田长安 , 刘俊亮 , 蔡 俊 , 曾燕伟 . 溶胶凝胶-自燃烧法合成La 9.33Si 6O26超细粉体[J]. 无机材料学报, 2008 , 23(1) : 77 -81 . DOI: 10.3724/SP.J.1077.2008.00077

Abstract

Single-phase and ultrafine La9.33Si6O26 powders were directly synthesized by a sol-gel self-combustion method using citric acid and ethylene alcohol as chelating reagents and fuels, nitrate as oxidant and ammonia to adjust the pH value of the system. XRD and TEM were employed for the phase identification and morphological observations of the obtained powders, which sintering performance was also studied. The results show that single-phase La.33Si6O26 powders with particles sizes ranging from 150nm to 300nm can be directly and rapidly synthesized through sol-gel and self-combustion processes without ary additional thermal solid reactions on the properly selected reaction conditions. The ultrafine powders possess very high sintering activities, and can be well sintered at 200℃ lower than the sintered temperature of the powders derived from conventional solid reactions.

参考文献

[1] Suda S, Mikio I, Eri N, et al. Journal of the European Ceramic Society, 2006, 26: 593-597.
[2] 扬乃涛, 孟秀霞, 谭小耀, 等(YANG Nai-Tao, et al). 无机材料学报(Journal of Inorganic Materials), 2006, 21 (2): 409-414.
[3] 田长安, 曾燕伟. 电源技术, 2006, 30 (4): 329-333.
[4] Lee D S, Kim W S, Choi S H, et al. Solid State Ionics, 2005, 176: 33-39.
[5] Panteix P J, Julien I, D. Bernache-Assollant, et al. Materials Chemistry and Physics, 2006, 95: 313-320.
[6] Susumu N, Masatomi S. Journal of the European Ceramic Society, 1998, 18 (10): 1413-1418.
[7] Hideki Y, Shigeo T. Solid State Ionics, 2005, 176: 2395-2398.
[8] Shaula A L, Kharton V V, Marques F M B. Journal of Solid State Chemistry, 2005, 178: 2050-2061.
[9] Tao S W, Irvine J T S. Materials Research Bulletin, 2001, 36: 1245-1258.
[10] Célérier S, Laberty C, Ansart F, et al. Ceramics International, 2006, 32 (3): 271-276.
[11] 付长璟, 孙克宁, 张乃庆, 等. 功能材料, 2006, 37 (6): 925-928.
[12] 程乐华, 王 敏, 陈永红. 应用化学, 2006, 23 (5): 561-565.
[13] 徐红梅, 严红革, 陈振华. 硅酸盐学报, 2006, 34 (4): 393-397.
[14] 张乃庆, 孙克宁, 朴金花, 等. 人工晶体学报, 2004, 33 (5): 758-761.
[15] Souza F L, Bueno P R, Longoa E, et al. Solid State Ionics, 2004, 166: 83-88.
[16] Leite E R, Carreno N L V, Longo E, et al. Chem. Mater., 2002, 14: 3722-3729.
[17] Hwang C C, Tsai J S, Huang T H, et al. Journal of Solid State Chemistry, 2005, 178: 382-389.
[18] 孟 波, 谭小耀, 杨乃涛, 等. 材料工程, 2005, 6: 31-35.
[19] 尧巍华, 张中太, 唐子龙, 等. 稀有金属材料与工程, 2004, 33 (4): 421-423.
[20] Ana M Segadǎes, Márco R Morelli, Ruth G A Kiminami. Journal of European Ceramic Society, 1998, 18 (7): 771-781.
[21] Sansom J E H, Richings D, Slater P R. Solid State Ionics, 2001, 139: 205-210.
文章导航

/