采用粒子溶出造孔法, 用棒状谷氨酸钠晶体作为造孔粒子, 制备磷酸钙骨水泥多孔支架, 研究了造孔粒子含量和多孔支架孔隙率之间的关系, 并加入甲壳素纤维来改善支架材料的力学性能. 结果表明, 支架材料的孔隙率可达(79.8±2.3)%,孔隙直径100～600μm; 复合纤维后支架的强度提高了3～4倍, 断裂应变显著提高, 可作为非承重部位骨缺损修复的骨组织工程支架材料.
Macroporous calcium phosphate cement (CPC) scaffold was prepared by a salt-leaching method using water-dissoluble rod-shaped monosodium glutamate crystals as poregen. The relationship between the porosity and the amount of poregen was investigated. The results indicate that the porosity of CPC scaffold come up to (79.8±2.3)% with a pore size range of 100--600μm. Chitin fibers was incorporated to reinforce CPC scaffold. The compressive strength of the Chitin fibers reinforced CPC scaffold increases 3 to 4 times higher than that of the CPC scaffold without fibers and the strain of fracture increases remarkably. The scaffold material may be applied in the bone tissue engineering for repair of non-load bearing bone defects.
[1] Takagi S, Chow L C. Journal of Materials Science : Materials in Medicine, 2001, 12: 135--139.
[2] Xu H H K, Takagi S, Quinn J B, et al. J. Biomed. Mater. Res., 2004, 68A: 725--734.
[3] 张利, 李玉宝, 周钢, 等(ZHANG Li, et al). 无机材料学报(Journal of Inorganic Materials), 2006, 21 (5): 1197--1202.
[4] Xu H H K, Eichmiller F C, Giuseppetti A A. J. Biomed. Mater. Res., 2000, 52: 107--114.
[5] Khairoun I, Driessens F C M, Boltong M G, et al. Biomaterials, 1999, 20: 393--398.
[6] Wei G, Ma P X. Biomaterials, 2004, 25: 4749--4757.
[7] Bovan B D, Hummert T W, Dean D D, et al. Biomaterials, 1996, 17: 137--146.
[8] Wang X P, Ye J D, Chen L, et al. Key Engineering Materials, 2007, 330-332: 983--986.
[9] 董浩, 叶建东, 王秀鹏. 功能材料, 2006, 37 (11): 1805--1809.
[10] 魏杰, 刘昌胜, 洪华, 等(WEI Jie, et al). 无机材料学报(Journal of Inorganic Materials), 2006, 21 (4): 958--964.
[11]肖长发.纤维复合材料-纤维、基体、力学性能. 第一版. 北京: 中国石化出版社. 1991. 6--14.
[12] 顾震隆. 短纤维复合材料力学. 第一版. 北京: 国防工业出版社. 1987. 163--172.