导电导磁改性短碳纤维的制备及电磁特性的研究

doi:10.3724/SP.J.1077.2010.00463

摘要/Abstract

摘要：

对短碳纤维进行氧化处理后,采用原位氧化沉淀聚合法使苯胺/磁流体或者苯胺/磁粉在其表面进行包覆反应,制备出具备有一定长径比的导电导磁改性短碳纤维.采用扫描电镜、X射线能谱及X射线衍射对改性碳纤维的形貌、化学组成进行了分析,利用PNA-LN5230A微波网络测试仪测定了其在频率2GHz以下的复介电常数和复磁导率,对比分析了两种不同方法制备的改性碳纤维的电磁参数以及2mm厚度下的吸收损耗.结果表明：聚苯胺/磁流体包覆的碳纤维（改性SCF-A）包覆层完整、致密,Fe含量为2.86at%;聚苯胺/磁粉包覆碳纤维（改性SCF-B）的包覆层外观完整、比较松散,Fe含量为3.12at%.改性SCF-A的复介电常数的实部大于改性SCF-B,但其虚部则小于改性SCF-B;改性SCF-B的复磁导率整体大于改性SCF-A.在频率2GHz以下,改性SCF-A的最大吸收损耗为3.06dB,改性SCF-B的最大吸收损耗为4.14dB.

关键词: 聚苯胺, 磁性物质, 短碳纤维, 电磁特性

Abstract:

Combined the nitric acid oxidation method and in-situ polymerization method were applied to prepare two kinds of electromagnetic modified short carbon fibers (SCF), coated with aniline/magnetic liquid and aniline/magnetic powder. The morphology and element contents of the modified SCF were investigated by using SEM, EDS and XRD. The complex permittivity and complex permeability of the modified SCF were measured by Agilent PNALN5230A microwave network analyzer in 50MHz-2GHz band. The absorption loss was simulated by Matlab6.5 software. SEM observation indicated the polyaniline/magnetic liquid coating of modified SCF was integrated and compact, but the polyaniline/magnetic powder coating of modified SCF was integrated and incompact. The Fe element contents of the polyaniline/magnetic liquid coated SCF (modified SCF-A) and polyaniline/magnetic powder coated SCF (modified SCF-B) were 2.86at% and 3.12at%, respectively. The real part of the complex permittivity of modified SCF-A was higher than that of modified SCF-B, on the contrary, the imaginary part of the complex permittivity and the complex permeability of the modified SCF-A were lower than that of the modified SCF-B. The absorption loss of modified SCF-A and modified SCF-B were 3.06dB and 4.14dB, respectively.

Key words: polyaniline, magnetic powder, short carbon fiber, electromagnetic properties

中图分类号:

TB332

喻冬秀. 导电导磁改性短碳纤维的制备及电磁特性的研究[J]. 无机材料学报, 2010, 25(5): 463-467.

YU Dong-Xiu. Preparation and Electromagnetic Characteristic of Magnetic and Conductive Modified Short Carbon Fibers[J]. Journal of Inorganic Materials, 2010, 25(5): 463-467.

参考文献

[1]Al-Saidy A H, Klaiber F W, Wipf T J. Strengthening of steel-concrete composite girders using carbon fiber reinforced polymer plates.Construction and Building Materials,2007, 21(2):295-302
[2]Keith Jason M, Janda Nicholas B, King Julia A, et al. Shielding effectiveness density theory for carbon fiber/nylon 6,6 Composites.Polymer Composites,2005, 26(5):671-678
[3]Tsotra P, Friedrich K. Short carbon fiber reinforced epoxy resin/polyaniline blends: their electrical and mechanical properties.Composites Science & Technology,2004, 64(15):2385-2391
[4]Tzeng Shinn-Shyong, Chang Fa-Yen. EMI shielding effectiveness of metal-coated carbon fiber-reinforced ABS composites.Materials Science and Engineering A,2001, 302(2):258-267
[5]Huang Chi-Yuan, Mo Wen-Wei. The effect of attached fragments on dense layer of electroless Ni/ P deposition on the electromagnetic interference shielding effectiveness of carbon fiber/acrylonitrile-butadienestyrene composites.Surface and Coatings Technology,2002, 154(1):55-62
[6]Huang Chi-Yuan, Mo Wen-Wei, Roan Ming-Lin. Studies on the influence of double-layer electroless metal deposition on the electromagnetic interference shielding effectiveness of carbon fiber/ABS composites.Surface Coatings Technology,2004, 184(2/3):163-169
[7]Yang Y, Zhang B S, Xu W D, et al. Preparation and electromagnetic characteristics of a novel ironcoated carbon fiber.Journal of Alloys and Compounds,2004, 365(8):300-302
[8]Huang ChiYuan, Mo WenWei, Roan MingLin. The influence of heat treatment on electrolessnickel coated fiber(ENCF) on the mechanical properties and EMI shielding of ENCF reinforced ABS polymer composites.Surface and Coatings Technology,2004,184(2/3):123-132
[9]邓建国, 贺传兰, 龙新平, 等. 磁性Fe3O4聚吡咯纳米微球的合成与表征.高分子学报,2003,(3):393-398
[10]Denga Jian-Guo, He Chuan-Lan, Peng Yu-Xing, et al. Magnetic and conductive Fe₃O₄-polyaniline nanoparticles with core-shell structure.Synthetic Metals,2003, 139(2):295-301
[11]Zhang Zhi-Ming, Wan Mei-Xiang. Nanostructures of polyaniline composites containing nano-magnetic.Synthetic Metals,2003, 132(2):205-212
[12]Del Castillo-Castro T, Larios-Rodriguez E, Molina-Arenas Z, et al. Synthesis and characterization of metallic nanoparticles and their incorporation into electro-conductive polymer composites.Composites: Part A,2007, 38(1):107-113
[13]Sugimoto S, Kondo S, Okayama K, et al. M-type ferrite composite as a microwave absorber with wide bandwidth in the GHz range.IEEE Transactions on Magnetic,1999, 35(5):3154-3156
[14]Du Jin-Hong, Chao Sun, ShuoBai, et al. Microwave electromagnetic characteristics of a microcoiled carbon fibers/paraffin wax composites in Kubana.J. Mater. Res,2002, 17(5):1232-1236
[15]程国娥, 黄开勋, 柯汉忠. 导电、导磁聚苯胺纳米复合物的合成与表征.地球科学——中国地质大学学报,2004, 29(1):65-68
[16]杨显清, 赵家升, 王园. 电磁场与电磁波. 北京：国防工业出版社, 2003: 7.
[17]喻冬秀, 陈明涛, 皮丕辉, 等. 聚苯胺包覆短碳纤维的制备及电磁性能研究.高校化学工程学报, 2009, 23（1）： 148-153.