微米铜粉/纳米TiO2复合粒子的低温制备及光吸收性能

doi:10.3724/SP.J.1077.2010.00370

摘要/Abstract

摘要： 利用仿生合成的方法在温和条件下制备了微米铜粉/纳米TiO₂复合粒子. 选择有机胺对Cu粉进行表面处理, XPS分析表明有机胺通过N原子与表面Cu²⁺络合形成功能层, 在Cu粉表面引入 NH₂和 OH等功能基团, 对比实验证实功能基团能够诱导无机氧化物的仿生沉积. XRD结果表明铜粉表面包覆的纳米TiO₂呈现锐钛矿晶型, 漫反射光谱（DRS）分析表明, Cu粉经过有机胺处理后在716.5nm处出现了由Cu²⁺离子与N配位产生的弱吸收. 复合粒子的光吸收性能介于TiO₂和Cu粉之间, Cu负载后样品的光吸收阀值从397.5nm红移至448.9nm, 红移的原因可归于Cu负载后TiO₂导带下出现新能级, 光生电子经过这些中间能级发生跃迁, 所需激发能量降低至可见光范围. 448.9nm处吸收边的存在表明复合粒子具备可见光催化活性.

关键词: 铜粉, 纳米TiO₂, 复合颗粒, 仿生合成

Abstract: Micron size Cu/nanoTiO₂composite particles were prepared in ambient conditions by bioinspired method. The surfaces of Cu particles were modified by a kind of amine, and the analysis of XPS indicated that the functional layer containing -NH₂and -OH groups was formed on the surface of Cu particles through the coordination of nitrogen in the amine to Cu²⁺. Comparative experiment confirmed that -NH₂ and -OH groups induced the biomineralization of nano-TiO₂on the Cu surfaces. XRD result showed that TiO₂ of anatase type was deposited on the surfaces of Cu particles. Results of diffuse reflectance spectra (DRS) showed that a weak absorption at 716.5nm occurred after Cu particles were modified by the amine, which indicated the coordination of N to Cu₂⁺. The photoabsorbance of Cu/nanoTiO₂ composite particles was between the photo-absorbance of TiO₂ and that of Cu. The optical absorption edge of the particles was extended from 397.5nm to about 448.9nm after Cu loading, because Cu loading introduces new mid gap level below the conduction band of TiO₂, and in this way the electron can be excited by visible light through the level. The absorption edge at 448.9nm indicated that Cu/nano-TiO₂composite particles had the visible light catalytic activity.

Key words: Cu powder, nano-TiO₂, composite particles, bio-inspired preparation

中图分类号:

TQ174

闫军,王彬,崔海萍,杜仕国. 微米铜粉/纳米TiO₂复合粒子的低温制备及光吸收性能[J]. 无机材料学报, DOI: 10.3724/SP.J.1077.2010.00370.

YAN Jun,WANG Bin,CUI Hai-Ping,DU Shi-Guo. Low Temperature Preparation and Photoabsorbance Property of Micron Size Cu/Nano-TiO₂ Composite Particles[J]. Journal of Inorganic Materials, DOI: 10.3724/SP.J.1077.2010.00370.

参考文献

[1］刘会景, 柏源, 孙红旗, 等(LIU Hui-Jing, et al). 掺杂基团对氮改性TiO₂紫外光催化活性影响的机理研究. 无机材料学报(Journal of Inorganic Materials), 2009, 24(3)：443-447.
［2］Lim S H, Phonthammachai N, Pramana S S, et al. Simple route to monodispersed silicatitania coreshell photocatalysts. Langmuir, 2008, 24(12)：6226-6231.
［3］Ao Y H, Xu J J, Fu D G, et al. Low temperature preparation of anatase TiO₂-coated activated carbon. Colloids and Surfaces A: Physicochem. Eng. Aspects, 2008, 312(2/3)：125130.
［4］Woan K, Pyrgiotakis G, Sigmund W. Photocatalytic carbonnanotubeTiO₂ composites. Advanced Materials, 2009, 21(1)：1-7.
［5］梅长松, 钟顺和, 肖秀芬. Cu/V₂O₅-TiO₂的结构、光吸收性能与催化反应性能研究. 功能材料, 2005, 36(2)：256-259.
［6］徐林林, 唐艳茹. 仿生物矿化过程合成无机/有机复合体研究. 长春师范学院学报(自然科学版), 2007, 26(1)：56-57.
［7］蔡国斌, 万勇, 俞书宏(CAI Guo-Bin, et al). 受生物启发模拟合成生物矿物材料及其机理研究进展. 无机化学学报(Chinese Journal of Inorganic Chemistry), 2008, 24(5)：673-683.
［8］Copello G J, Varela F, Martinez Vivot R, et al. Immobilized chitosan as biosorbent for the removal of Cd(Ⅱ), Cr(Ⅲ) and Cr(Ⅵ) from aqueous solutions. Bioresource Technology, 2008, 99(14)：6538-6544.
［9］Becker T, Schlaak M, Strasdeit H. Adsorption of nickel(Ⅱ), zinc(Ⅱ) and cadmium(Ⅱ) by new chitosan derivatives. Reactive & Functional Polymers, 2000, 44(3)：289-298.
［10］闫军, 杜仕国, 崔海萍, 等(YAN Jun, et al). 涂覆Mannich碱对Cu粉抗氧化性能的影响. 金属学报(Acta Metallurgica Sinica), 2007, 43(4)：388-392.
［11］Sagiv J. Organized monolayers by adsorption. 1. Formation and structure of oleophobic mixed monolayers on solid surfaces. Journal of the American Chemical Society, 1980, 102（1）：92-98.
［12］Sá J, Agüera C A, Gross S. et al. Photocatalytic nitrate reduction over metal modifed TiO₂. Applied Catalysis B: Environmental, 2009, 85(3/4)：192-200.
［13］Yang R N, Li C Y, Liu Y F. et al. Synthesis and structure of copper(Ⅱ) complex ［Cu(C₅H₅N)₂(H₂O)(C₆H₅COO)₂］. Chinese J. Struct. Chem., 2001, 20(1)：4-7.
［14］Aranda P, Kun R, MartínLuengo M. A, et al. Titaniasepiolite nanocomposites prepared by a surfactant templating colloidal route. Chem. Mater., 2008, 20(1)：84-91.
［15］尹荔松, 沈辉, 张进修. 纳米TiO₂粉晶的光学特性研究.电子学报, 2002, 30(6)：808-810.
［16］周时凤, 洪樟连, 赵芙蓉, 等(ZHOU Shi-Feng, et al). 一种可见光响应纳米TiO₂粉体的光响应特性表征. 无机材料学报(Journal of Inorganic Materials), 2006, 21(4)：783-788.
［17］丁开宁. 金属修饰TiO₂(110)表面的电子结构和表面态的理论研究. 福州：福州大学博士论文, 2005.
［18］Bao L L, Mahurin S M, Dai S. Controlled layerbylayer formation of ultrathin TiO₂ on silver island films via a surface Sol-Gel method for surfaceenhanced raman scattering measurement. Anal. Chem., 2004, 76(15)：4531-4536.

[1]	李永生, 陈玲. 可控制备磁性四氧化三铁-金纳米复合颗粒及其催化性能研究[J]. 无机材料学报, 2018, 33(2): 221-228.
[2]	翟云刚, 董文杰, 高勇平, 牛德超, 陈健壮, 顾金楼, 李永生, 施剑林. 超顺磁金纳米壳复合颗粒的粒径调控及其诊疗应用[J]. 无机材料学报, 2015, 30(9): 950-956.
[3]	刘刚, 黄婉霞, 易勇. λ-Ti₃O₅粉体的制备及其光存储性能的研究[J]. 无机材料学报, 2013, 28(4): 425-430.
[4]	王岳俊, 周康根, 蒋志刚. 加料方式对超细氧化亚铜粉体分散性与粒度稳定性的影响[J]. 无机材料学报, 2012, 27(2): 195-200.
[5]	胡宾, 潘卉, 余来贵, 王龙阁, 赵磊, 张治军. 水杨酸原位表面改性纳米TiO₂的制备及性能研究[J]. 无机材料学报, 2011, 26(11): 1181-1186.
[6]	冯炜, 邹克华, 翟增秀. 微波辅助低温制备纳米TiO₂晶体生长动力学研究[J]. 无机材料学报, 2010, 25(8): 815-819.
[7]	刘宇,张颋,傅敏恭,李旺,杜国平. 高压微波合成纳米TiO₂及其光催化性能[J]. 无机材料学报, 2010, 25(4): 375-378.
[8]	张继远,田汉民,田志鹏,王湘艳,于涛,邹志刚. TiO₂纳米晶溶胶水热的合成及其染料敏化光电性能[J]. 无机材料学报, 2009, 24(6): 1110-1114.
[9]	杜昶,王迎军. 骨与牙釉质组织的生物矿化及磷酸钙材料仿生合成研究进展[J]. 无机材料学报, 2009, 24(5): 882-888.
[10]	周民杰,曾振欧,钟理,赵国鹏. 纳米TiO₂/Sb₂O₅涂层的光生阴极保护研究[J]. 无机材料学报, 2009, 24(3): 525-530.
[11]	王江,左奕,杨维虎,周钢,张利,李玉宝. 纳米羟基磷灰石丝素蛋白仿生矿化材料的制备研究[J]. 无机材料学报, 2009, 24(2): 264-268.
[12]	李秀艳,杨贤锋,吴明Mei. 不同介质中水热合成纳米TiO₂粉体及其光催化性能研究[J]. 无机材料学报, 2008, 23(6): 1253-1258.
[13]	罗民,程佳,马晶,陈小,王斌鉴,杨建锋. 仿生制备多孔氮化硅陶瓷[J]. 无机材料学报, 2008, 23(4): 763-768.
[14]	许龙山,陈小华,陈传盛,李文华,杨植. 碳纳米管-超细铜粉复合粉体的制备[J]. 无机材料学报, 2006, 21(2): 309-314.
[15]	姚超,高国生,林西平2,杨绪杰,陆路德,汪信. 掺杂氧化铝对金红石相纳米TiO₂微结构和光催化活性的影响[J]. 无机材料学报, 2006, 21(1): 58-64.

微米铜粉/纳米TiO₂复合粒子的低温制备及光吸收性能

Low Temperature Preparation and Photoabsorbance Property of Micron Size Cu/Nano-TiO₂ Composite Particles

PDF (PC)

可视化

被引次数

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

编辑推荐

Metrics

本文评价