激光铝热还原法制备Al2O3/Ti-Al基复合涂层

doi:10.3724/SP.J.1077.2013.12730

无机材料学报 ›› 2013, Vol. 28 ›› Issue (9): 1033-1039.DOI: 10.3724/SP.J.1077.2013.12730 CSTR: 32189.14.SP.J.1077.2013.12730

激光铝热还原法制备Al₂O₃/Ti-Al基复合涂层

张晓伟, 刘洪喜, 蒋业华, 范氏红娥

(昆明理工大学材料科学与工程学院, 昆明 650093)

收稿日期:2012-12-03 修回日期:2013-01-08 出版日期:2013-09-20 网络出版日期:2013-08-14
作者简介:张晓伟(1984-), 男, 博士研究生. E-mail: zhxw72@163.com
基金资助:
国家自然科学基金(51261013); 昆明理工大学分析测试基金(2010025, 2011008)

Microstructure of Al₂O₃/Ti-Al Composite Coatings Prepared by Laser Aluminum Thermal Reduction Processing

ZHANG Xiao-Wei, LIU Hong-Xi, JIANG Ye-Hua, PHAM THI Hong-Nga

(Faculty of Materials Science and Engineering, Kunming University of Science and Technology, Kunming 650093, China)

Received:2012-12-03 Revised:2013-01-08 Published:2013-09-20 Online:2013-08-14
About author:ZHANG Xiao-Wei. E-mail: zhxw72@163.com
Supported by:
National Natural Science Foundation of China(51261013); Analysis and Testing Foundation of KMUST(2010025, 2011008)

摘要/Abstract

摘要： 利用Al和TiO₂之间的放热化学反应, 采用激光原位合成技术在TC4钛合金基体材料表面制备了Al₂O₃/Ti-Al金属间化合物基复合涂层。对比分析了激光功率、激光束扫描速度和光斑尺寸变化对激光能量密度变化量的影响程度, 借助X射线衍射仪(XRD)、光学显微镜(OM)、能谱仪(EDS)和显微硬度计分别考察了激光束扫描速度对复合涂层表面宏观形貌、截面显微组织结构和显微硬度的影响。结果显示, 扫描速度的变化对激光能量密度变化量的影响程度最大, 光斑尺寸次之, 激光功率的变化影响最弱。随着激光束扫描速度的增大, 复合涂层表面渐趋粗糙, “鱼鳞纹”状形貌特征趋于明显, 复合涂层与基材结合区厚度减小。激光原位复合涂层主要由k-Al₂O₃和α-Al₂O₃增强相与α-Ti和α₂-Ti₃Al基体相组成。随着激光束扫描速度增大, 复合涂层内k-Al₂O₃部分转变为α-Al₂O₃, Al₂O₃增强相有由枝晶状向纤维状转变的趋势; 复合涂层截面显微硬度自基体至涂层表面过度平缓, 且涂层区显微硬度分布均匀, 明显高于基材平均显微硬度。

关键词: 激光熔覆, 原位合成, 铝热还原, Al₂O₃/Ti-Al基复合涂层, TC4钛合金

Abstract: With composite powders of Al and TiO₂ systems as reactants, Al₂O₃ reinforced Ti-Al matrix intermetallic composite coatings were prepared on the TC4 alloy substrate by laser in-situ synthesis processing. The effects of laser power, laser scanning speed and laser spot size on laser energy density were analyzed, respectively. The macroscopic morphology, cross-section microstructure, and micro-hardness of Al₂O₃/Ti-Al composite coatings were characterized by optical microscope (OM), X-ray diffraction (XRD), energy dispersive spectroscope (EDS) and micro-hardness tester. The results show that scanning speed has the greatest impact on laser energy density firstly, then the laser spot size, and then the weakest is laser power. With the scanning speed increases, Al₂O₃/Ti-Al composite coatings surface become rougher, “fish-scale shape” morphology are more obvious, and the thickness of bonding-zone decreases. The reinforced phase of composite coating is composed of k-Al₂O₃ and α-Al₂O₃, while the matrix phase is composed of α-Ti and α₂-Ti₃Al. And with the increase of laser scanning speed, k-Al₂O₃changes into α-Al₂O₃ partially. The morphology of Al₂O₃ reinforcement tends to change from dendrite shape to fiber. The micro-hardness of samples has a smooth transition tendency from the substrate to the coating surface. The micro-hardness distribution of coating cross section is uniform, and the average micro-hardness is significantly higher than that of the substrate.

Key words: laser cladding, in-situ synthesis, aluminothermic reduction, Al₂O₃/Ti-Al composite coating, TC4 alloy

中图分类号:

TB333

张晓伟, 刘洪喜, 蒋业华, 范氏红娥. 激光铝热还原法制备Al₂O₃/Ti-Al基复合涂层[J]. 无机材料学报, 2013, 28(9): 1033-1039.

ZHANG Xiao-Wei, LIU Hong-Xi, JIANG Ye-Hua, PHAM THI Hong-Nga. Microstructure of Al₂O₃/Ti-Al Composite Coatings Prepared by Laser Aluminum Thermal Reduction Processing[J]. Journal of Inorganic Materials, 2013, 28(9): 1033-1039.

参考文献

[1] WANG H M, CAO F, CAI L X, et al. Microstructure and tribological properties of laser clad Ti2Ni3Si/NiTi intermetallic coatings. Acta Mater., 2003, 51(20): 6319-6327.

[2] ZHANG X W, LIU H X, Wang C Q, et al. Microstructure and high temperature oxidation resistance of TiN/Ti3Al intermetallic composite coatings on Ti6Al4V alloy by laser cladding. Proc. SPIE, 2010, 7843: 21.

[3] ALLEN C, BLOYCET A, BELLT T. Sliding wear behaviour of ion implanted ultra high molecular weight polyethylene against a surface modified titanium alloy Ti-6Al-4V. Tribol. Int., 1996, 29(6): 527-534.

[4] LENG C Y, ZHOU R, ZHANG X, et al. Wear performance of Ti6Al4V alloy modified by Ag+Ta dual-ion impantation. Acta Metall. Sin., 2009, 45(6): 764-768.

[5] YUE L Y, WANG Z B, LI L. Material morphological characteristics in laser ablation of alpha case from titanium alloy. Appl. Surf. Sci., 2012, 258(20): 8065-8071.

[6] WU C F, MA M X, LIU W J, et al.. Study on wear resistance of laser caldding Fe-based composite coatings reinforced by in-situ multiple carbide particles. Acta Metall. Sin., 2009, 45(8): 1013-1018.

[7] GUO B G, ZHOU J S, ZHANG S T, et al. Microstructure and tribological properties of in situ synthesized TiN/Ti3Al intermetallic matrix composite coatings on titanium by laser cladding and laser nitriding. Mat. Sci. Eng. A, 2008, 480(1/2): 404-410.

[8] LIANG J, GAO M Y, LIU C S, et al. Laser induced in-situ formation of titanium composite coatings. Chinese Journal of Laser, 2009, 36(12): 3272-3276.

[9] MAN H C, ZHANG S, CHENG F T, et al. In situ synthesis of TiC reinforced surface MMC on Al6061 by laser surface alloying. Scripta Mater., 2002, 46(3): 229-234.

[10] 江东亮, 李龙土, 欧阳世翕, 等. 中国材料工程大典: 无机非金属材料工程(上), 第8卷. 北京: 化学工业出版社, 2005: 35.

[11] RUPPI S, LARSSON A. Chemical vapour deposition of κ-Al 2O3. Thin Solid Films, 2001, 388(1/2): 50-61.

[12] BARBATTI C, GARCIA J, PITONAK R, et al. Influence of micro-blasting on the microstructure and residual stresses of CVD κ-Al2O3 coatings. Surf. Coat. Technol., 2009, 203(24): 3708-3717.

[13] ZHANG X W, LIU H X, JIANG Y H, et al. Research progress of functional composite coatings on Ti6Al4V alloy surface prepared by laser cladding technique. Rare Metal Materials and Engineering, 2012, 41(1): 178-183.

[14] AI T T, WANG F, FENG X M, et al. Microstructure and mechanical properties of in situ Al2O3 particles reinforced two-phase TiAl-based composites. The Chinese Journal of Nonferrous Metals, 2007, 17(11): 1849-1854.

[15] AI T T. Microstructures and mechanical properties of in-situ Al2O3/TiAl composites by exothermic dispersion method. Acta Metall. Sin., 2008, 21(6): 437-443.

[16] XIANG L Y, WANG F, ZHU J F, et al. Mechanical properties and microstructure of Al2O3/TiAl in situ composites doped with Cr2O3. Mat. Sci. Eng. A, 2000, 528(9): 3337-3341.

[17] LI Z Q, QU W, HAN J C, et al. Investigation on combustion synthesis and reaction process of Al-Ti-TiO2 system. Journal of Inorganic Materials, 2002, 17(2): 293-298.

[18] FENG C F, FROYEN L. Formation of Al3Ti and Al2O3 from an Al-TiO2 system for preparing in-situ aluminium matrix composites. Compos. Part A-Appl. S., 2000, 31(4): 385-390.

[19] TJONG S C, MA Z Y. Microstructural and mechanical characteristics of in situ metal matrix composites. Mat. Sci. Eng. R, 2000, 29(3/4): 49-113.

[20] LIANG S Q, ZHENG Z Q. The microstructure analyses of the combustion wave in Al-TiO2 system by self-propagation high temperature synthesis (SHS). Rare Metal Materials and Engineering, 1993, 22(4): 42-45.

[21] AI T T. Microstructure and mechanical properties of in-situ synthesized Al2O3/TiAl composites. Chinese. J. Aeronaut., 2008, 21(6): 559-564.

[22] 李荣久. 陶瓷-金属复合材料, 2版. 北京: 冶金工业出版社, 2004: 12, 21, 24.

[23] WANG F, XU H Y, ZHU J F, et al. Ho-doped Al2O3/TiAl composites fabricated by in-situ reaction synthesis. Powder Metallurgy Technology, 2010, 28(1): 34-38.

[24] ZHANG X W, LIU H X, JIANG Y H, et al. Laser in situ synthesized TiN/Ti3Al composite coatings. Acta Metall. Sin., 2011, 47(8): 1086-1093.

[25] 李俊昌. 激光的衍射及热作用计算(修订版). 北京: 科学出版社, 2008: 394.

[26] 师昌绪, 李恒德, 周廉. 材料科学与工程手册. 北京: 化学工业出版社, 2004: 284.

[27] SEIFERT H J, KUSSMAUL A, ALDINGER F. Phase equilibria and diffusion paths in the Ti-Al-O-N system. J. Alloys Compd., 2001, 317-318: 19-25.

[28] 周公度, 段连运. 结构化学基础, 3版. 北京: 北京大学出版社, 2002: 178.

激光铝热还原法制备Al₂O₃/Ti-Al基复合涂层

Microstructure of Al₂O₃/Ti-Al Composite Coatings Prepared by Laser Aluminum Thermal Reduction Processing

RichHTML

PDF (PC)

可视化

被引次数

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 11

编辑推荐

Metrics

本文评价

[1]	褚颖, 李云伟, 吴启兵, 胡静, 田千秋, 户赫龙, 朱永平. 高导电性热电池正极材料Ni-NiCl₂复合物的原位合成与放电性能研究[J]. 无机材料学报, 2016, 31(9): 992-996.
[2]	潘建梅, 程晓农, 严学华, 张成华, 徐桂芳. 多孔SiCO陶瓷中SiC纳米线的原位合成及生长机理[J]. 无机材料学报, 2013, 28(5): 474-478.
[3]	刘建华, 张施露, 于美, 安军伟, 李松梅. 石墨烯接枝聚吡咯复合物的原位合成及其电容特性研究[J]. 无机材料学报, 2013, 28(4): 403-408.
[4]	孙培秋, 朱德贵, 蒋小松, 孙红亮, 夏兆辉. 原位合成TiB₂-TiC_0.8-SiC复相陶瓷的微观组织与性能研究[J]. 无机材料学报, 2013, 28(4): 363-368.
[5]	郭纯, 周健松, 陈建敏. 钛表面激光熔覆原位制备Ti₅Si₃涂层结构及摩擦学性能[J]. 无机材料学报, 2012, 27(9): 970-976.
[6]	卢翠英, 殷小玮, 李向明. 渗硅技术原位制备Ti₃SiC₂-SiC复合材料的新工艺[J]. 无机材料学报, 2010, 25(9): 1003-1008.
[7]	顾巍, 杨建, 丘泰, 祝社民. 原位合成(TiB₂+TiC)/Ti₃SiC₂复相材料及其性能研究[J]. 无机材料学报, 2010, 25(10): 1081-1086.
[8]	宗丽,刘莹,辛峰. 整体式堇青石载体上 TS-1的原位合成[J]. 无机材料学报, 2007, 22(6): 1227-1232.
[9]	刘淑霞,贺军辉. 人发的无机复制及金纳米粒子的原位合成[J]. 无机材料学报, 2006, 21(6): 1313-1318.
[10]	刘见芬,蒋引珊,王安平,宋波. 蒙脱石原位合成高热稳定性Al-MCM-41[J]. 无机材料学报, 2003, 18(4): 867-871.
[11]	邹正光,陈寒元,麦立强. 钛铁矿原位碳热还原合成TiC/Fe的热力学过程及合成条件研究[J]. 无机材料学报, 2001, 16(5): 903-908.